Description: PLEXIGLAS® XT extruded acrylic
تفاصيل
تطبيقات
منتج
المورد
مزايا
- absolutely colorless
- clear break-resistant to impact-resistant
- unequalled resistance to weathering and ageing
- very good surface
- brilliant
- textured or satin
- good resistance to dilute acids
- limited resistance to organic solvents
- good resistance to alkalis
- easy to work
- similar to hardwood
- easy to thermoform under optimal constant conditions
- easily bonded also with solvent adhesives
- burns more or less like hardwood
- very little smoke generation
- max. service temperature approx. 70 °C
تطبيقات أخرى
sheets, tubes, round rods, multi-skin sheets, corrugated sheets, mirror sheets1.5 to 25 mm solid sheet thickness
multi-skin sheets 16 mm and 32 mm thick standard size up to 4050 x 2050 mm (+ extra lengths)more than 25 standard colors
معلومات تقنية
كمية | قدر | وحدة | التعلیق |
---|---|---|---|
خصائص المظهر | |||
Refractive index | 1.491 | clear grade; ISO 489@Thickness 3.00 mm | |
الخصائص الفيزيائية | |||
Density | 1.19 | g/ml | ISO 1183 |
الخصائص الحرارية | |||
U Value | 5.6 | W/m² | DIN 4701; for 3 mm |
Specific Heat Capacity | 1.47 | J/gºC | |
Heat Deflection temperature | 100 | ºC | ISO 75;at 0.46 MPa |
Heat Deflection temperature | 95.0 | ºC | ISO 75;at 1.8 MPa |
Maximum Service Temperature | 70.0 | ºC | Permanent;Air |
Vicat softening temperature | 103 | ºC | ISO 306, Method B 50 |
Thermal Expansion | 70.0 | µm/m-°C | DIN 53752A@Temperature 0.000-50.0 °C;linear |
U Value | 4.4 | W/m² | DIN 4701; for 10 mm |
U Value | 5.8 | W/m² | DIN 4701; for 1 mm |
U Value | 5.3 | W/m² | DIN 4701; for 5 mm |
Thermal Conductivity | 0.190 | W/mk | DIN 52612 |
flash point | 430 | ºC | Ignition Temperature; DIN 51794 |
Maximum Service Temperature | 180 | ºC | IR Radiator |
خصائص ميكانيكية | |||
Abrasion | 20 - 30 | Haze, Abrasion resistance in Taber abrader test (100 rev.;5.4 N; CS-10F); ISO 9352 | |
(Izod impact strength(notched | 1.60 | kJ/m² | ISO 180/1A |
(Charpy Impact Strength(unnotched | 15.0 | kJ/m² | ISO 179/1fU |
Ball indentation Hardness | 175 | MPa | H961/30; ISO 2039-1 |
Flexural strength | 105 | MPa | 5mm/min (80x10x4 mm); ISO 178 |
Tensile Stress at break-MD | 72.0 | MPa | ISO 527-2/1B/5 |
Tensile modulus-MD | 3300 | MPa | Short Time Value; ISO 527-2/1B/1 |
Elongation at break-MD | 4.5 | % | ISO 527-2/1B/5 |
Poisson's ratio | 0.37 | dilation speed of 5% per min; up to 2% dilation; ISO 527-1@Temperature 23.0 °C | |
shear modulus | 1700 | MPa | Dynamic Shear Modulus at 10 Hz; ISO 537 |
Tensile Stress at break-MD | 100 | MPa | ISO 527-2/1B/5@Temperature -40.0 °C |
Coefficient of friction | 0.50 | plastic/steel | |
Compressive Strength | 103 | MPa | ISO 604; at Yield |
Tensile strength | 35.0 | MPa | ISO 527-2/1B/5@Temperature 70.0 °C;Ultimate |
Coefficient of friction | 0.45 | steel/plastic | |
Coefficient of friction | 0.80 | plastic/plastic | |
الخواص الكيميائية | |||
Moisture Expansion | 0.50 | % | Possible Expansion due to heat and moisture |
Water absorption | 2.1 | % | Max. Weight Gain During Immersion; ISO 62, Method 1; at Saturation |
Water absorption | 0.44 | % | 24 hrs, 23°C from dry state; ISO 62, Method 1 |
Moisture Vapor Transmission | 55 | cc-mm/m²-24hr-atm | |
Permeability | 8.3e-15 | g cm/cm2 h Pa | to Air |
Permeability | 1.1e-13 | g cm/cm2 h Pa | to CO2 |
Permeability | 4.5e-15 | g cm/cm2 h Pa | to N2 |
Permeability | 2.0e-14 | g cm/cm2 h Pa | to O2 |
الخواص البصرية | |||
Transmittance | 80 | % | UV; clear grade@Thickness 3.00 mm |
Transmittance | 92 | % | Visible; clear grade; DIN 5036, Part 3@Thickness 3.00 mm |
Absorption in the Visible Range | <0.05 | % | clear grade, 3 mm |
Transmittance | 85 | % | Total Energy Transmittance g; clear grade, 3 mm, DIN EN 410 |
Reflection Coefficient | 0.040 | Visible (0-1); clear grade, Reflection loss in the visible range (for each surface) @Thickness 3.00 mm | |
الخواص الكهربائية | |||
Volume resistance | >1.00e+15 | ohm-cm | DIN VDE 0303, Part 3 |
Surface Resistance | 5.00e+13 | ohm | DIN VDE 0303, Part 3 |
Dielectric Strength | 30.0 | Kv/mm | DIN VDE 0303, Part 2 |
Comparative Tracking Index | 600 | V | DIN VDE 0303, Part 1 |
Shielding Effectiveness | 26 | dB | Weighted Sound Reduction Index at 4 mm |
Shielding Effectiveness | 32 | dB | Weighted Sound Reduction Index at 10 mm |
Shielding Effectiveness | 30 | dB | Weighted Sound Reduction Index at 6 mm |
Dielectric Constant | 2.8 | DIN VDE 0303, Part 4@Frequency 100000 Hz | |
Dielectric Constant | 3.7 | DIN VDE 0303, Part 4@Frequency 50 Hz | |
Dissipation Factor | 0.030 | DIN VDE 0303, Part 4@Frequency 100000 Hz | |
Dissipation Factor | 0.060 | DIN VDE 0303, Part 4@Frequency 50 Hz |