Injection Molding, PC/ABS, Heat Resistance, High Flow, High Impact.
تفاصيل
CAS
103598-77-2 , 9003-56-9
صناعة
منتج
مزايا
- high heat resistance
- high impact strength
تطبيقات أخرى
Automotive (Interior)
E&E (housing)
معلومات تقنية
كمية | قدر | وحدة | التعلیق |
---|---|---|---|
الخصائص الفيزيائية | |||
Humidity | <0.02 | % | injection molding |
Specific Gravity | 1.14 | ASTM D792 | |
Linear Mold Shrinkage | 0.005 - 0.008 | cm/cm | ASTM D955 |
MFI | 5.3 | g/10min | ASTM D 1238 , Temperature 250 °C -Load 2.16 kg |
الخصائص الحرارية | |||
UL RTI | 60 | ºC | Electrical-Thickness 3- mm |
UL RTI | 60 | ºC | Electrical-Thickness 1.6- mm |
Heat Deflection temperature | 113 | ºC | ASTM D648 |
Dry Time | 240 - 360 | min | Injection Molding |
UL RTI | 60 | ºC | Mechanical with Impact-Thickness 1.6- mm |
UL RTI | 60 | ºC | Mechanical with Impact-Thickness 3- mm |
UL RTI | 60 | ºC | Mechanical without Impact-Thickness 1.6- mm |
UL RTI | 60 | ºC | Mechanical without Impact-Thickness 3- mm |
Flameability | Thickness 1.6- mm | ||
Flameability | Thickness 3- mm | ||
خصائص ميكانيكية | |||
Rockwell Hardness | 114 | ASTM D 785 | |
Flexural modulus-MD | 2108.42 | MPa | ASTM D 790 |
Flexural strength | 77.47 | MPa | ASTM D 790 |
Tensile strength | 56.87 | MPa | ASTM D638 |
Elongation at break-MD | >100 | % | ASTM D638 |
الخواص الكهربائية | |||
HAI)High Amp Arc Ignition) | >150 | arcs | |
Arc Resistance | 60 - 120 | s | ASTM D 495 |
خصائص العملية | |||
Middle Barrel Temperature | 245 - 275 | ºC | injection molding |
Drying Temperature | 80 - 100 | ºC | injection molding |
Mold Temperature | 50 - 70 | ºC | injection molding |