starex® TX-0510T is a transparent acrylonitrile butadiene styrene (ABS) grade. Can be processed using injection molding.
Details
Product Type
Applications
Industry
Producer
Advantages
- excellent balance of transparency, mechanical properties, & processability
- excellent color consistency & stability
Other Applications
Households products/ Consumer Goods > Toys
Packaging >food containers
Electronics / Computers > TV housings
Appliances > dust box of vacuum cleaner
Appliances > washing machine top cover
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Appearance Properties | |||
Appearance | |||
Physical state | Pill | ||
Physical Properties | |||
Humidity | <0.05 | % | |
MFI | 16 | g/10min | ISO 1133;220℃/10kg |
Density | 1.1 | g/ml | ISO 1183 |
Thermal Properties | |||
Vicat softening temperature | 88 | ºC | ISO R 306;B/50 |
Heat Deflection temperature | 86 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Annealing |
Heat Deflection temperature | 80 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Annealing |
Dry Time | 120 - 240 | min | |
UL RTI | 50 | ºC | Mechanical without Impact, 1.5 mm, 3.0 mm |
UL RTI | 50 | ºC | Mechanical with Impact, 1.5 mm, 3.0 mm |
UL RTI | 50 | ºC | Electric, 1.5 mm, 3.0 mm |
Heat Deflection temperature | 83 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
Heat Deflection temperature | 70 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
Mechanical Properties | |||
Rockwell Hardness | 110 | ISO 2039-2;R Scale | |
Charpy Impact Strength (notched) | 13 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
(Izod impact strength(notched | 12 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
Flexural modulus-MD | 2200 | MPa | ISO 178;2mm/min |
Flexural strength | 70 | MPa | ISO 178;2mm/min |
Tensile Stress at break-MD | 35 | MPa | ISO 527;50mm/min |
Tensile modulus-MD | 2200 | MPa | ISO 527;50mm/min |
Strain at break-MD | 16 | % | ISO 527;50mm/min |
Tensile Stress at yield-MD | 47 | MPa | ISO 527;50mm/min |
Chemical Properties | |||
Decomposition temperature | >400 | ºC | |
Optical Properties | |||
Haze | 2.8 | % | ISO 13468;3.2 mm |
Transmittance | 88 | % | ISO 13468;3.2 mm |