Технические документы
Детали Соединение
Тип продукта
Усиленный с
зая́вки
Режиссер
поставщиком
Технические данные
Количество | Стоимость | Е диница измерения | 3амечание |
---|---|---|---|
Физические свойства | |||
Melting range | 221 - 226 | ºC | DSC |
MFI | 13.68 | g/10min | ISO 1133@Load 2.16 kg, Temperature 250 °C |
Linear Mold Shrinkage | 0.014 | cm/cm | Pigmentation can change mold shrinkage.;Transverse |
Linear Mold Shrinkage | 0.0015 | cm/cm | Pigmentation can change mold shrinkage. |
Density | 1.71 | g/ml | ISO 1183 |
Тепловые свойства | |||
Flameability | @Thickness 1.60 mm | ||
Flameability | @Thickness 0.800 mm | ||
Vicat softening temperature | 220 | ºC | 10N; ISO 306 |
Vicat softening temperature | 215 | ºC | 50N; ISO 306 |
Heat Deflection temperature | 215 | ºC | ISO 75-1/2;at 1.8 MPa |
Heat Deflection temperature | 223 | ºC | ISO 75-1/2;at 0.46 MPa |
Thermal Expansion | 40.0 | µm/m-°C | ISO 11359@Temperature 23.0 - 55.0 °C; Transverse to Flow |
Thermal Expansion | 40.0 | µm/m-°C | Longitudinal; ISO 11359@Temperature 23.0 - 55.0 °C |
Механические свойства | |||
Charpy Impact Strength (notched) | 12 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
(Charpy Impact Strength(unnotched | 65 | kJ/m² | ISO 179/1eU@Temperature -30.0 °C |
Charpy Impact Strength (notched) | 13 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |
(Charpy Impact Strength(unnotched | 60 | kJ/m² | ISO 179/1eU@Temperature 23.0 °C |
Tensile modulus-MD | 15000 | MPa | ISO 527-1/2 |
Elongation at break-MD | 1.8 | % | 5 mm/min; ISO 527-1/2 |
Tensile Stress at break-MD | 180 | MPa | 5 mm/min; ISO 527-1/2 |
Ball indentation Hardness | 230 | MPa | H30; ISO 2039-1 |
Hardness Shore D | 85 | ISO 868 | |
Химические свойства | |||
Electrolytic Corrosion | IEC 60426 | ||
Oxirane Oxygen Content | 20 | % | ISO 4589 |
Water absorption | 0.40 | % | ISO 62;at Saturation |
Электрические свойства | |||
Comparative Tracking Index | 525 | V | Test Solution A, CTI; IEC 60112 |
Volume resistance | 1.00e+15 | ohm-cm | IEC 60093 |
Dielectric Constant | 4.5 | IEC 60250@Frequency 100 Hz | |
Surface Resistance | 1.00e+13 | ohm | IEC 60093 |
Dielectric Constant | 4.9 | IEC 60250@Frequency 1e+6 Hz | |
Dissipation Factor | 0.0040 | IEC 60250@Frequency 100 Hz | |
Dissipation Factor | 0.015 | IEC 60250@Frequency 1e+6 Hz | |
Dielectric Strength | 27.0 | Kv/mm | K20/P50; IEC 60243-1 |
Comparative Tracking Index | 500 | V | Test Solution A, 100 drops; IEC 60112 |