الوثائق الفنية
CYREX 300 alloy is suitable for applications where a high degree of heat resistance is necessary.
تفاصيل
تطبيقات
منتج
المورد
مزايا
- high degree of heat resistance
معلومات تقنية
كمية | قدر | وحدة | التعلیق |
---|---|---|---|
الخصائص الفيزيائية | |||
Linear Mold Shrinkage | 0.0040 - 0.0080 | cm/cm | ASTM D551 |
MFI | 1.9 | g/10min | ASTM D1238@Load 3.80 kg, Temperature 230 °C |
Specific Gravity | 1.17 | ASTM D792 | |
الخصائص الحرارية | |||
Vicat softening temperature | 152 | ºC | ASTM D1525 |
Heat Deflection temperature | 123 | ºC | ASTM D648; at 1.8 MPa |
Thermal Expansion | 93.6 | µm/m-°C | ASTM D696@Temperature 0.000 -100 °C;Linear |
Flameability | |||
خصائص ميكانيكية | |||
Flexural strength | 91.7 | MPa | ASTM D790 |
Elongation at yield | 4.7 | % | ASTM D638 |
Rockwell Hardness | 55 | Rockwell M; ASTM D785 | |
Tensile modulus-MD | 2200 | MPa | ASTM D638 |
Tensile Stress at yield-MD | 62.7 | MPa | ASTM D638 |
Elongation at break-MD | 73 | % | ASTM D638 |
Izod impact strength (notched) | 838 | J/m | Thickness 3.17 mm, Temperature 22.8 °C@ |
Flexural modulus-MD | 2300 | MPa | ASTM D790 |
Izod impact strength (notched) | 566 | J/m | Thickness 6.35 mm, Temperature 22.8 °C@ |
الخواص الكيميائية | |||
Water absorption | <0.26 | % | ASTM D570 |