INFINO® HM-1100F is a halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy reinforced with 10 % glass fiber. Can be processed using injection molding.
تفاصيل مركب
نوع المنتج
تطبيقات
صناعة
منتج
مزايا
- high impact strength & modulus
- high flowability
- good colorability
- excellent appearance
- well-balanced mechanical properties & processability
- halogen free
- flame retardant
تطبيقات أخرى
Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter
معلومات تقنية
كمية | قدر | وحدة | التعلیق |
---|---|---|---|
خصائص المظهر | |||
Physical state | Pill | ||
Appearance | Natural colors | ||
الخصائص الفيزيائية | |||
Density | 1.25 | g/ml | ISO 1183 |
Shrinkage | 0.1 - 0.2 | % | (ISO 2577;Flow, 3.2 mm (MD |
Shrinkage | 0.1 - 0.2 | % | (ISO 2577;Cross Flow, 3.2 mm (TD |
MFI | 26 | g/10min | ISO 1133;220℃/10kg |
MFI | 8 | g/10min | ISO 1133;250℃/2.16kg |
Humidity | <0.04 | % | |
الخصائص الحرارية | |||
Heat Deflection temperature | 94 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
Heat Deflection temperature | 95 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
Dry Time | 180 - 240 | min | |
UL RTI | 60 | ºC | Mechanical without Impact, 1.5 mm, 2.0 mm, 3.0 mm |
UL RTI | 60 | ºC | Electric, 1.5 mm, 2.0 mm, 3.0 mm |
UL RTI | 60 | ºC | Mechanical with Impact, 1.5 mm, 2.0 mm, 3.0 mm |
Vicat softening temperature | 98 | ºC | ISO R 306;B/50 |
Glass transition Temperature | 98 | ºC | DSC |
خصائص ميكانيكية | |||
Tensile Stress at yield-MD | 80 | MPa | ISO 527;5mm/min |
Strain at break-MD | 4 | % | ISO 527;5mm/min |
Tensile modulus-MD | 3400 | MPa | ISO 527;5mm/min |
Tensile Stress at break-MD | 85 | MPa | ISO 527;5mm/min |
Flexural strength | 100 | MPa | ISO 178;2mm/min |
Flexural modulus-MD | 4000 | MPa | ISO 178;2mm/min |
(Izod impact strength(notched | 8 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
Charpy Impact Strength (notched) | 7 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
Rockwell Hardness | 118 | ISO 2039-2;R Scale | |
الخواص الكيميائية | |||
Decomposition temperature | >400 | ºC |