INFINO® HM-1157 is a halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) grade reinforced with glass fiber. Can be processed using injection molding.
تفاصيل مركب
نوع المنتج
تطبيقات
صناعة
منتج
مزايا
- high impact strength & modulus
- high flowability
- good colorability
- excellent appearance
- well-balanced mechanical properties & processability
- halogen free
- flame retardant
تطبيقات أخرى
Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter
معلومات تقنية
كمية | قدر | وحدة | التعلیق |
---|---|---|---|
خصائص المظهر | |||
Appearance | Natural colors | ||
Physical state | Pill | ||
الخصائص الفيزيائية | |||
Humidity | <0.04 | % | |
MFI | 25 | g/10min | ISO 1133;250℃/2.16kg |
Density | 1.28 | g/ml | ISO 1183 |
الخصائص الحرارية | |||
UL RTI | 60 | ºC | Electric, 1.5 mm, 3.0 mm |
UL RTI | 60 | ºC | Mechanical with Impact, 1.5 mm, 3.0 mm |
UL RTI | 60 | ºC | Mechanical without Impact, 1.5 mm, 3.0 mm |
Heat Deflection temperature | 91 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
خصائص ميكانيكية | |||
Tensile Stress at break-MD | 90 | MPa | ISO 527;5mm/min |
Strain at break-MD | 4 | % | ISO 527;5mm/min |
Tensile modulus-MD | 3800 | MPa | ISO 527;5mm/min |
Flexural modulus-MD | 4800 | MPa | ISO 178;2mm/min |
(Izod impact strength(notched | 5 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
Charpy Impact Strength (notched) | 5 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
Flexural strength | 120 | MPa | ISO 178;2mm/min |
Tensile Stress at yield-MD | 90 | MPa | ISO 527;5mm/min |
الخواص الكيميائية | |||
Decomposition temperature | >400 | ºC |