INFINO® LM-1090 is a luminous, halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy. Can be processed using injection molding.
تفاصيل
نوع المنتج
تطبيقات
صناعة
منتج
مزايا
- high impact strength & modulus
- high flowability
- good colorability
- excellent appearance
- well-balanced mechanical properties & processability
- halogen free
- flame retardant
- luminous
تطبيقات أخرى
Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter
معلومات تقنية
كمية | قدر | وحدة | التعلیق |
---|---|---|---|
خصائص المظهر | |||
Appearance | Natural colors | ||
Physical state | Pill | ||
الخصائص الفيزيائية | |||
Humidity | <0.05 | % | |
MFI | 25 | g/10min | ISO 1133;250℃/2.16kg |
MFI | 58 | g/10min | ISO 1133;220℃/10kg |
Shrinkage | 0.6 | % | (ASTM D955;Cross Flow, 3.2 mm (TD |
Shrinkage | 0.6 - 0.7 | % | (ASTM D955;Flow, 3.2 mm (MD |
Density | 1.2 | g/ml | ISO 1183 |
الخصائص الحرارية | |||
Dry Time | 120 - 240 | min | |
Heat Deflection temperature | 100 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
UL RTI | 60 | ºC | Mechanical without Impact, 1.5 mm, 3.0 mm |
UL RTI | 60 | ºC | Mechanical with Impact, 1.5 mm, 3.0 mm |
UL RTI | 60 | ºC | Electric, 1.5 mm, 3.0 mm |
Vicat softening temperature | 100 | ºC | ISO R 306;B/50 |
Heat Deflection temperature | 87 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
خصائص ميكانيكية | |||
Rockwell Hardness | 122 | ISO 2039-2;R Scale | |
Charpy Impact Strength (notched) | 5 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
(Izod impact strength(notched | 5 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
Flexural modulus-MD | 2350 | MPa | ISO 178;2.8mm/min |
Flexural strength | 85 | MPa | ISO 178;2.8mm/min |
Tensile Stress at break-MD | 600 | MPa | ISO 527;50mm/min |
Tensile Stress at yield-MD | 60 | MPa | ISO 527;50mm/min |
Strain at break-MD | 60 | % | ISO 527;50mm/min |
Tensile modulus-MD | 2100 | MPa | ISO 527;50mm/min |
الخواص الكيميائية | |||
Decomposition temperature | >400 | ºC |