Injection Molding Grade, PC/ABS+CNT, Electrostatic Dissipation, High Flow, Good Processability
تفاصيل مركب
CAS
7440-44-0
تطبيقات
منتج
معلومات تقنية
كمية | قدر | وحدة | التعلیق |
---|---|---|---|
الخصائص الفيزيائية | |||
Humidity | <0.01 | % | |
Specific Gravity | 1.21 | ASTM D792 | |
Linear Mold Shrinkage | 0.004 - 0.006 | cm/cm | Thickness 3.2 mm |
الخصائص الحرارية | |||
Flameability | Thickness 3.2- mm | ||
Flameability | Thickness 2.5- mm | ||
Flameability | Thickness 1.6- mm | ||
Flameability | Thickness 0.8- mm | ||
UL RTI | 60 | ºC | Mechanical without Impact |
UL RTI | 60 | ºC | Mechanical with Impact |
UL RTI | 60 | ºC | Electrical |
Heat Deflection temperature | 250 | ºC | |
Dry Time | 180 - 300 | min | |
Thermal Conductivity | 1.7 | W/mk | Laser flash method |
خصائص ميكانيكية | |||
Izod impact strength (notched) | 19.6 | J/m | Thickness 3.2 mm |
Flexural strength | 127.48 | MPa | Thickness 6.4 mm |
Flexural modulus-MD | 12944.77 | MPa | Thickness 6.4 mm |
Tensile strength | 73.55 | MPa | Thickness 3.2 mm |
Elongation at break-MD | >5 | % | Thickness 3.2 mm |
الخواص الكهربائية | |||
Volume resistance | 1e+016 | ohm-cm | |
Surface Resistance | 1.000E+006 - 1.000E+009 | ohm | IEC 60093 |
خصائص العملية | |||
Mold Temperature | 130 - 150 | ºC | |
Middle Barrel Temperature | 310 - 320 | ºC | |
Drying Temperature | 120 - 140 | ºC |