Injection Molding, PC/ABS, Halogen Free Flame Retardant, EPEAT
تفاصيل
CAS
9003-56-9
تطبيقات
منتج
معلومات تقنية
كمية | قدر | وحدة | التعلیق |
---|---|---|---|
الخصائص الفيزيائية | |||
Humidity | <2 | % | |
Specific Gravity | 1.18 | ||
MFI | 18 | g/10min | 250°C/2.16Kg |
Linear Mold Shrinkage | 0.004 - 0.006 | cm/cm | Thickness 3.2 mm |
الخصائص الحرارية | |||
Flameability | Thickness 3- mm | ||
Flameability | Thickness 1.5- mm | ||
UL RTI | 60 | ºC | Mechanical without Impact |
UL RTI | 60 | ºC | Electrical |
UL RTI | 60 | ºC | Mechanical with Impact |
Dry Time | 180 - 240 | min | |
خصائص ميكانيكية | |||
Izod impact strength (notched) | >490 | J/m | Thickness 3.2 mm |
Flexural modulus-MD | 2549.72 | MPa | Thickness 6.4 mm |
Flexural strength | 93.16 | MPa | Thickness 6.4 mm |
Tensile strength | 58.84 | MPa | Thickness 3.2 mm |
Elongation at break-MD | 30 | % | Thickness 3.2 mm |
خصائص العملية | |||
Middle Barrel Temperature | 240 - 255 | ºC | |
Mold Temperature | 50 - 80 | ºC | |
Drying Temperature | 75 - 85 | ºC |