Injection Molding, PC/ABS, Halogen Free Flame Retardant, High Flow
تفاصيل
CAS
9003-56-9
تطبيقات
منتج
معلومات تقنية
كمية | قدر | وحدة | التعلیق |
---|---|---|---|
الخصائص الفيزيائية | |||
Humidity | <2 | % | |
Specific Gravity | 1.18 | ||
Linear Mold Shrinkage | 0.004 - 0.006 | cm/cm | Thickness 3.2 mm |
MFI | 21 | g/10min | 250°C/2.16Kg |
الخصائص الحرارية | |||
UL RTI | 60 | ºC | Mechanical without Impact-Thickness 2- mm |
UL RTI | 60 | ºC | Mechanical without Impact-Thickness 1.5- mm |
UL RTI | 60 | ºC | Mechanical with Impact-Thickness 3- mm |
UL RTI | 60 | ºC | Mechanical with Impact-Thickness 2- mm |
UL RTI | 60 | ºC | Mechanical with Impact-Thickness 1.5- mm |
UL RTI | 60 | ºC | Electrical-Thickness 3- mm |
UL RTI | 60 | ºC | Electrical-Thickness 2- mm |
UL RTI | 60 | ºC | Electrical-Thickness 1.5- mm |
Dry Time | 240 - 360 | min | |
UL RTI | 60 | ºC | Mechanical without Impact-Thickness 3- mm |
Flameability | Thickness 1.5- mm | ||
Flameability | Thickness 2- mm | ||
Flameability | Thickness 3- mm | ||
Flameability | Thickness 2- mm | ||
Heat Deflection temperature | 85 | ºC | |
خصائص ميكانيكية | |||
Izod impact strength (notched) | J/m | Thickness 3.2 mm | |
Flexural modulus-MD | 2647.79 | MPa | Thickness 6.4 mm |
Flexural strength | 87.27 | MPa | Thickness 6.4 mm |
Tensile strength | 54.91 | MPa | Thickness 3.2 mm |
Elongation at break-MD | >50 | % | Thickness 3.2 mm |
خصائص العملية | |||
Middle Barrel Temperature | 215 - 250 | ºC | |
Mold Temperature | 50 - 80 | ºC | |
Drying Temperature | 60 - 80 | ºC |