Injection Molding, PC/ABS+GF20%, Halogen Free Flame Retardant, High Stiffness
تفاصيل مركب
CAS
9003-56-9
تطبيقات
منتج
معلومات تقنية
كمية | قدر | وحدة | التعلیق |
---|---|---|---|
الخصائص الفيزيائية | |||
Humidity | <4 | % | |
Specific Gravity | 1.36 | ||
MFI | 11 | g/10min | 250°C/2.16Kg |
Linear Mold Shrinkage | 0.002 - 0.004 | cm/cm | Thickness 3.2 mm |
الخصائص الحرارية | |||
Flameability | Thickness 2- mm | ||
Flameability | Thickness 1.5- mm | ||
Flameability | Thickness 2- mm | ||
UL RTI | 60 | ºC | Mechanical without Impact-Thickness 2- mm |
UL RTI | 60 | ºC | Mechanical without Impact-Thickness 1.5- mm |
UL RTI | 60 | ºC | Mechanical with Impact-Thickness 2- mm |
UL RTI | 60 | ºC | Mechanical with Impact-Thickness 1.5- mm |
UL RTI | 60 | ºC | Electrical-Thickness 2- mm |
UL RTI | 60 | ºC | Electrical-Thickness 1.5- mm |
Dry Time | 180 - 240 | min | |
خصائص ميكانيكية | |||
Izod impact strength (notched) | 108 | J/m | Thickness 3.2 mm |
Flexural modulus-MD | 5884 | MPa | Thickness 3.2 mm |
Tensile strength | 102.97 | MPa | Thickness 3.2 mm |
Flexural strength | 147.10 | MPa | Thickness 3.2 mm |
Elongation at break-MD | 5 | % | |
خصائص العملية | |||
Middle Barrel Temperature | 245 - 265 | ºC | |
Mold Temperature | 60 - 80 | ºC | |
Drying Temperature | 75 - 85 | ºC |