Razalen® Q111 is a natural colored, general purpose polypropylene (PP) homopolymer grade. It is suitable for processing by injection molding. Used in various industrial and high performance applications.
تفاصيل
نوع المنتج
تطبيقات
منتج
التركيب الكيميائي
polypropylene (PP) homopolymer
مزايا
- General purpose
تطبيقات أخرى
various industrial and high performance applications
معلومات تقنية
كمية | قدر | وحدة | التعلیق |
---|---|---|---|
dry Time | 1 - 2 | hr | |
Processing Temperature | 200 - 230 | ºC | |
خصائص المظهر | |||
Physical state | Granulated | ||
Appearance | Natural colors | ||
الخصائص الفيزيائية | |||
Shrinkage | 1.5 | % | ASTM D955; Linear |
MFI | 25 | g/10min | ASTM D1238;230°C, 2.16 kg |
Density | 0.9 | g/ml | ASTM D792 |
الخصائص الحرارية | |||
Vicat softening temperature | 152 | ºC | ASTM D 1525 |
Heat Deflection temperature | 95 | ºC | ASTM D648;at 66 psi (0.46 MPa), Unannealed |
خصائص ميكانيكية | |||
(Izod impact strength(notched | 3 | kJ/m² | ASTM D256; at 23°C |
Flexural modulus-MD | 1500 | MPa | ASTM D790 |
Flexural strength | 40 | MPa | ASTM D790 |
Elongation at break-MD | 13 | % | ASTM D638 |
Tensile Stress at yield-MD | 32 | MPa | ASTM D638 |
خصائص العملية | |||
Drying Temperature | 80 - 100 | ºC | |
Middle Barrel Temperature | 200 - 220 | ºC | |
Mold Temperature | 30 - 60 | ºC |