Razalen® R133TR5 is a rubber modified, dark grey colored, high impact polypropylene (PP) grade. It is suitable for processing by injection molding. Used in automotive applications such as bumper.
تفاصيل
نوع المنتج
تطبيقات
منتج
التركيب الكيميائي
polypropylene (PP)
مزايا
- rubber modified
- excellent toughness
- good processability
- chemical and UV resistance
- high impact
تطبيقات أخرى
automotive applications such as bumper
معلومات تقنية
كمية | قدر | وحدة | التعلیق |
---|---|---|---|
Processing Temperature | 220 - 260 | ºC | |
dry Time | 2 - 4 | hr | |
خصائص المظهر | |||
Physical state | Granulated | ||
Appearance | |||
الخصائص الفيزيائية | |||
Shrinkage | 1 | % | ASTM D955; Linear |
MFI | 12 | g/10min | ASTM D1238;230°C, 2.16 kg |
Density | 0.93 | g/ml | ASTM D792 |
الخصائص الحرارية | |||
Heat Deflection temperature | 85 | ºC | ASTM D648;at 0.46 MPa;Unannealed |
خصائص ميكانيكية | |||
(Izod impact strength(notched | kJ/m² | ASTM D256; at 23°C | |
Flexural modulus-MD | 650 | MPa | ASTM D790 |
Flexural strength | 23 | MPa | ASTM D790 |
Elongation at break-MD | >100 | % | ASTM D638 |
Tensile Stress at yield-MD | 17 | MPa | ASTM D638 |
خصائص العملية | |||
Mold Temperature | 30 - 60 | ºC | |
Middle Barrel Temperature | 190 - 220 | ºC | |
Drying Temperature | 80 - 100 | ºC |