الوثائق الفنية
TROGAMID® CX compounds round off the product range of High Performance Polymers to include semi-crystalline polyamides, the crystallites of which are so small that they do not scatter visible light-a property known as microcrystallinity. The compounds are therefore as clear as glass. Areas of application can be as diverse as water management, filter technology, laboratory and medical technology, the manufacture of eyeglasses, or bottles for the cosmetics industry.Specific Notes for this Material: Highly viscous, permanently transparent polyamide for extrusion, with an external mold release agent.
تفاصيل
microcrystallinity semi-crystalline polyamides
- crystal-clear
- permanent transparency
- high transmission
- superior chemical resistance
- stress cracking resistance
- high level of UV resistance
- low water absorption
- high dimensional stability
- balanced mechanical property profile
- high impact resistance, even at low temperatures
- high level of dynamic strength (e.g., for internally pressurized parts)
- abrasion and scratch resistance
- high glass transition temperature
- very low isotropic shrinkage
- easy processing
- High Performance
filter technology
laboratory and medical technology
the manufacture of eyeglasses
bottles for the cosmetics industry
معلومات تقنية
كمية | قدر | وحدة | التعلیق |
---|---|---|---|
الخصائص الفيزيائية | |||
Density | 1.02 | g/ml | ISO 1183 |
الخصائص الحرارية | |||
Glow WireTest | 850 | ºC | IEC 60695-2-1/0-3, Thickness 1 mm |
Maximum Service Temperature | 100 | ºC | Temperature Index (Criterion: stress and yield); IEC 216 |
Heat Deflection temperature | 110 | ºC | (ISO 75-1/2, 1.8 MPa (264 psi |
Glass transition Temperature | 140 | ºC | Tg, 10 K/min |
Heat Deflection temperature | 126 | ºC | (ISO 75-1/2, 0.46 MPa (66 psi |
Thermal Expansion | 90 | µm/m-°C | Longitudinal; ISO 11359, Temperature 23-80 °C, linear |
Flameability | Thickness 1.6 mm , UL94 | ||
Vicat softening temperature | 129 | ºC | 50N; ISO 306 |
Flameability | Thickness 0.8 mm, UL94 | ||
Melting point | 250 | ºC | 10K/min |
Vicat softening temperature | 136 | ºC | 10N; ISO 306 |
Thermal Expansion | 90 | µm/m-°C | Transverse to Flow, ISO 11359, Temperature 23-80 °C |
خصائص ميكانيكية | |||
Tensile strength | 60 | MPa | at Yield, 50 mm/min ; ISO 527-1/2 |
Tensile strength | >50 | MPa | 50mm/min ; ISO 527-1/2, at Break |
Elongation at break-MD | >150 | % | 50mm/min ; ISO 527-1/2 |
Creep modulus | 700 | MPa | ISO 899-1,1000 hour |
Hardness Shore D | 81 | ISO 868 | |
Flexural strength | 90 | MPa | 5mm/min; ISO 178 |
Flexural strength | 50 | MPa | 5mm/min, at 3.5% Strain; ISO 178 |
Flexural modulus-MD | 1700 | MPa | ISO 178 |
(Charpy Impact Strength(unnotched | 99990 | kJ/m² | ISO 179/1eU, Temperature 0 °C |
(Charpy Impact Strength(unnotched | 99990 | kJ/m² | ISO 179/1eU, Temperature -30°C |
(Charpy Impact Strength(unnotched | 99990 | kJ/m² | ISO 179/1eU, Temperature 23°C |
Ball indentation Hardness | 108 | MPa | H30; ISO 2039-1 |
Tensile strength | >50 | MPa | |
Tensile modulus-MD | 1500 | MPa | ISO 527-1/2 |
Charpy Impact Strength (notched) | 17 | kJ/m² | ISO 179/1eA, Temperature 0 °C |
Elongation at yield | 9 | % | 5mm/min, Outer fiber strain at maximum stress; ISO 178 |
Charpy Impact Strength (notched) | 16 | kJ/m² | ISO 179/1eA, Temperature -30°C |
Charpy Impact Strength (notched) | 18 | kJ/m² | ISO 179/1eA, Temperature 23°C |
Elongation at yield | 8 | % | 50mm/min ; ISO 527-1/2 |
viscosity number | 180 - 200 | ml/g | ISO 307 |
Creep modulus | 1400 | MPa | ISO 899-1,1 hour |
الخواص الكهربائية | |||
Dissipation Factor | IEC 60250 DIN VDE 0303-Part 4, Frequency 100 Hz | ||
Dissipation Factor | IEC 60250 DIN VDE 0303-Part 4, Frequency 1000000 Hz | ||
Dielectric Constant | 3.2 | IEC 60250 DIN VDE 0303-Part 4, Frequency 1000000 Hz | |
Dielectric Strength | 27 | Kv/mm | K20/P50; IEC 60243-1 |
Dielectric Constant | 3.6 | IEC 60250 DIN VDE 0303-Part 4, Frequency 100 Hz | |
Surface Resistance | >1.000E+013 | ohm | IEC 60093 |
Surface Resistance | >1.000E+015 | ohm | Spec.; IEC 60093 |
Comparative Tracking Index | 575 | V | Test Solution A, 100 drops; IEC 60112 |
Volume resistance | >1.000E+017 | ohm-cm | IEC 60093 |