VESTAKEEP® 4000 GF30 is a self-lubricating, semi-crystalline, self-extinguishing, high viscosity polyether ether ketone (PEEK) resin reinforced with 30% chopped glass fiber. It can be processed by injection molding and extrusion. Suitable for use in housing parts. Complies with FDA, UL flammability and EU (10/2011) regulations.
تفاصيل مركب
نوع المنتج
منتج
المورد
مزايا
- xcellent mechanical-, thermal- & chemical resistance
- high rigidity
- partially low warpage
- non-combustible
- recyclable
معلومات تقنية
| كمية | قدر | وحدة | التعلیق |
|---|---|---|---|
| خصائص المظهر | |||
| Physical state | Pill shape | ||
| الخصائص الفيزيائية | |||
| Shrinkage | 0.3 | % | ISO 294-4, 2 mm, Flow |
| MFI | 3 | g/10min | 380°C/5 kg- ISO 1133 |
| Density | 1.5 | g/ml | ISO 1183- 23°C |
| Shrinkage | 0.6 | % | ISO 294-4, 2 mm, Transverse |
| Melting range | 380 - 400 | ºC | |
| الخصائص الحرارية | |||
| Glass transition Temperature | 152 | ºC | |
| Flameability | UL 94, 1.6 mm | ||
| Heat Deflection temperature | 312 | ºC | ISO 75-1, 1.8 MPa, Method A |
| Vicat softening temperature | 340 | ºC | ISO 306, 10N, Method A |
| Heat Deflection temperature | 335 | ºC | ISO 75-1, 0.45 MPa, Method B |
| Melting point | 340 | ºC | ISO 11357, DSC - 2nd heating |
| Vicat softening temperature | 335 | ºC | ISO 306, 50N, Method B |
| Dry Time | 240 | min | |
| خصائص ميكانيكية | |||
| (Charpy Impact Strength(unnotched | 75 | kJ/m² | ISO 179/1eU, -30°C, Complete Break |
| (Charpy Impact Strength(unnotched | 70 | kJ/m² | ISO 179/1eU, 23°C, Complete Break |
| Charpy Impact Strength (notched) | 10 | kJ/m² | ISO 179/1eA, 23°C, Complete break |
| Strain at break-MD | 2 | % | ISO 527-2 |
| Tensile Stress at yield-MD | 165 | MPa | ISO 527-1 |
| Tensile modulus-MD | 11000 | MPa | |
| Charpy Impact Strength (notched) | 9 | kJ/m² | ISO 179/1eA, -30°C, Complete break |
| الخواص الكيميائية | |||
| LOI | 45 | % | ISO 4589, 3.2 mm |
| Water absorption | 0.4 | % | ISO 62, 23°C, Saturation |
| الخواص الكهربائية | |||
| Surface Resistance | ohm | IEC 60093 | |
| Volume resistance | ohm-cm | IEC 60093 | |
| Dissipation Factor | 0.004 | IEC 60250, 1 MHz | |
| Comparative Tracking Index | 200 | V | IEC 60112, Test solution A |
| Relative permittivity | 3.3 | IEC 60250, 1 MHz | |
| خصائص العملية | |||
| Mold Temperature | 160 - 200 | ºC | |
| Die Temperature | 400 | ºC | |
| Drying Temperature | 160 | ºC | |