| كمية | قدر | وحدة | التعلیق |
|---|---|---|---|
| الخصائص الفيزيائية | |||
| Linear Mold Shrinkage | 0.016 | cm/cm | Transverse |
| Linear Mold Shrinkage | 0.02 | cm/cm | sheet with film gate at rim, mold temperature 80°C@Thickness 2.00 mm |
| MFI | 18.34 | g/10min | ISO 1133@Load 2.16 kg,Temperature 250 °C |
| Density | 1.31 | g/ml | ISO 1183 |
| الخصائص الحرارية | |||
| Vicat softening temperature | 220 | ºC | Method A, 10 N; ISO 306 |
| Thermal Expansion | 110 | µm/m-°C | Transverse to Flow; ISO 11359, DIN 53752@Temperature 23.0-55.0 °C |
| Flameability | @Thickness 1.60 mm | ||
| Flameability | @Thickness 0.800 mm | ||
| Heat Deflection temperature | 55.0 | ºC | ISO 75-1/2-at 1.8 MPa |
| Heat Deflection temperature | 160 | ºC | ISO 75-1/2-at 0.46 MPa |
| Thermal Expansion | 110 | µm/m-°C | Longitudinal; ISO 11359, DIN 53752@Temperature 23.0-55.0 °C |
| Vicat softening temperature | 190 | ºC | Method B, 50 N; ISO 306 |
| خصائص ميكانيكية | |||
| Elongation at yield | 8.0 | % | ISO 527-1/2 |
| Hardness Shore D | 77 | ISO 868 | |
| Tensile Stress at yield-MD | 60.0 | MPa | ISO 527-1/2 |
| Tensile modulus-MD | 2600 | MPa | ISO 527-1/-2 |
| Elongation at break-MD | <50 | % | ISO 527-1/2 |
| (Charpy Impact Strength(unnotched | 200 | kJ/m² | ISO 179/1eU@Temperature -30.0 °C |
| (Charpy Impact Strength(unnotched | 220 | kJ/m² | ISO 179/1eU@Temperature 23.0 °C |
| Charpy Impact Strength (notched) | 5.5 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |
| Charpy Impact Strength (notched) | 5.5 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
| الخواص الكيميائية | |||
| Electrolytic Corrosion | IEC 60426 | ||
| Water absorption | 0.50 | % | ISO 62 -at Saturation |
| الخواص الكهربائية | |||
| Comparative Tracking Index | 600 | V | Test Solution A CTI; IEC 60112 |
| Comparative Tracking Index | 575 | V | 100 drops value; IEC 60112 |
| Dissipation Factor | 0.021 | IEC 60250@Frequency 1e+6 Hz | |
| Surface Resistance | 1.00e+14 | ohm | IEC 60093 |
| Volume resistance | 1.00e+15 | ohm-cm | IEC 60093 |
| Dielectric Constant | 3.5 | IEC 60250@Frequency 1e+6 Hz | |
| Dielectric Constant | 3.3 | IEC 60250@Frequency 100 Hz | |
| Dielectric Strength | 27.0 | Kv/mm | K20/P50; IEC 60243-1 |
| Dissipation Factor | 0.0015 | IEC 60250@Frequency 100 Hz | |