كمية | قدر | وحدة | التعلیق |
---|---|---|---|
الخصائص الفيزيائية | |||
Density | 1.60 | g/ml | |
MFI | 10 | g/10min | |
الخصائص الحرارية | |||
UL RTI | 140 | ºC | Mechanical without Impact |
UL RTI | 130 | ºC | Mechanical with Impact |
UL RTI | 130 | ºC | Electrical |
Flameability | @Thickness 1.60 mm | ||
Vicat softening temperature | 210 | ºC | 50°C/hr/50 N |
Heat Deflection temperature | 210 | ºC | at 1.8 MPa |
Heat Deflection temperature | 220 | ºC | at 0.46 MPa |
Thermal Expansion | <50 | µm/m-°C | @Temperature 20.0 °C |
Flameability | @Thickness 3.20 mm | ||
خصائص ميكانيكية | |||
Creep modulus | 7000 | MPa | 1000hours |
Creep modulus | 7500 | MPa | 1hour |
Charpy Impact Strength (notched) | 7 | kJ/m² | @Temperature -30.0 °C |
Charpy Impact Strength (notched) | 8 | kJ/m² | |
(Charpy Impact Strength(unnotched | 45 | kJ/m² | @Temperature -30.0 °C |
(Charpy Impact Strength(unnotched | 45 | kJ/m² | |
Tensile modulus-MD | 7500 | MPa | |
Elongation at break-MD | 2.0 | % | |
Tensile strength | 130 | MPa | |
Tensile Impact strength | 55.0 | Kj/m² | |
الخواص الكيميائية | |||
Moisture absorption | <0.50 | % | Humidity Absorption-at Equilibrium |
Water absorption | 0.000 | % | |
الخواص الكهربائية | |||
Dielectric Strength | 27.0 | Kv/mm | |
Dissipation Factor | 0.0030 | @Frequency 100 Hz | |
Dielectric Constant | 3.0 | @Frequency 100 Hz | |
Dielectric Constant | 4.0 | @Frequency 1e+6 Hz | |
Surface Resistance | 1.00e+14 | ohm | |
Electrical Resistivity | >1.00e+15 | ohm-cm | |
Dissipation Factor | 0.015 | @Frequency 1e+6 Hz | |
Comparative Tracking Index | 225 | V |