| كمية | قدر | وحدة | التعلیق |
|---|---|---|---|
| الخصائص الفيزيائية | |||
| MFI | 4 | g/10min | |
| Density | 1.66 | g/ml | |
| الخصائص الحرارية | |||
| Thermal Expansion | <50.0 | µm/m-°C | Transverse to Flow@Temperature 20.0 °C |
| Heat Deflection temperature | 160 | ºC | at 1.8 MPa |
| Thermal Expansion | <50.0 | µm/m-°C | Parallel to Flow@Temperature 20.0 °C |
| Heat Deflection temperature | 190 | ºC | at 0.46 MPa |
| Vicat softening temperature | 165 | ºC | 50°C/hr/50 N |
| Flameability | @Thickness 3.20 mm | ||
| Flameability | @Thickness 1.60 mm | ||
| خصائص ميكانيكية | |||
| Creep modulus | 6800 | MPa | 1hour |
| Tensile Impact strength | 8 | Kj/m² | |
| Tensile Stress at yield-MD | 120 | MPa | |
| Elongation at break-MD | 5.0 | % | |
| Elongation at yield | 3.0 | % | |
| Tensile modulus-MD | 7000 | MPa | |
| Charpy Impact Strength (notched) | 14 | kJ/m² | |
| (Charpy Impact Strength(unnotched | 60 | kJ/m² | |
| (Charpy Impact Strength(unnotched | 60 | kJ/m² | @Temperature -30.0 °C |
| Charpy Impact Strength (notched) | 10 | kJ/m² | @Temperature -30.0 °C |
| Creep modulus | 5100 | MPa | 1000hours |
| الخواص الكيميائية | |||
| Moisture absorption | <0.50 | % | at Equilibrium |
| Water absorption | 0.00 | % | |
| الخواص الكهربائية | |||
| Electrical Resistivity | >1.00e+15 | ohm-cm | |
| Surface Resistance | 1.00e+14 | ohm | |
| Dielectric Constant | 3.0 | @Frequency 1e+6 Hz | |
| Dielectric Constant | 4.0 | @Frequency 100 Hz | |
| Dielectric Strength | 25.0 | Kv/mm | |
| Dissipation Factor | 0.010 | @Frequency 100 Hz | |
| Dissipation Factor | 0.018 | @Frequency 1e+6 Hz | |
| Comparative Tracking Index | 225 | V | |