نوع المنتج
منتج
المورد
معلومات تقنية
كمية | قدر | وحدة | التعلیق |
---|---|---|---|
الخصائص الفيزيائية | |||
Density | 1.31 | g/ml | ISO 1183 |
Linear Mold Shrinkage | 0.015 | cm/cm | sheet with film gate at rim, mold temperature 80°C @Thickness 2.00 mm |
Linear Mold Shrinkage | 0.015 | cm/cm | Transverse |
MFI | 209.6 | g/10min | ISO 1133@Load 2.16 kg, Temperature 250 °C |
الخصائص الحرارية | |||
Heat Deflection temperature | 150 | ºC | ISO 75-1/-2;at 0.46 MPa |
Heat Deflection temperature | 55.0 | ºC | ISO 75-1/-2;at 1.8 MPa |
Vicat softening temperature | 190 | ºC | Method B, 50 N; ISO 306 |
Vicat softening temperature | 220 | ºC | Method A, 10 N; ISO 306 |
Flameability | IEC 60695@Thickness 1.60 mm | ||
Flameability | IEC 60695@Thickness 0.800 mm | ||
Thermal Expansion | 110 | µm/m-°C | Longitudinal; ISO 11359, DIN 53752 @Temperature 23.0 - 55.0 °C |
Thermal Expansion | 110 | µm/m-°C | ISO 11359, DIN 53752 @Temperature 23.0 - 55.0 °C ;Transverse to Flow |
خصائص ميكانيكية | |||
Tensile Stress at break-MD | 55.0 | MPa | ISO 527-1/2 |
Tensile modulus-MD | 2600 | MPa | ISO 527-1/-2 |
Elongation at break-MD | 5.0 | % | ISO 527-1/2 |
(Charpy Impact Strength(unnotched | 50 | kJ/m² | ISO 179/1eU@Temperature 23.0 °C |
(Charpy Impact Strength(unnotched | 40 | kJ/m² | ISO 179/1eU@Temperature -30.0 °C |
Charpy Impact Strength (notched) | 3 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |
Charpy Impact Strength (notched) | 2.5 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
Hardness Shore D | 80 | ISO 868 | |
Elongation at yield | 7.0 | % | Outer fiber strain at maximum stress, 5 mm/min; ISO 178 |
Flexural strength | 70.0 | MPa | at 3.5% strain, 5 mm/min; ISO 178 |
Flexural strength | 90.0 | MPa | 5 mm/min; ISO 178 |
الخواص الكيميائية | |||
Water absorption | 0.50 | % | ISO 62;at Saturation |
الخواص الكهربائية | |||
Dissipation Factor | 0.0020 | IEC 60250@Frequency 100 Hz | |
Dielectric Constant | 3.5 | IEC 60250@Frequency 1e+6 Hz | |
Volume resistance | 1.00e+17 | ohm-cm | IEC 60093 |
Surface Resistance | 1.00e+13 | ohm | IEC 60093 |
Dielectric Constant | 3.3 | IEC 60250@Frequency 100 Hz | |
Dissipation Factor | 0.023 | IEC 60250@Frequency 1e+6 Hz | |
Comparative Tracking Index | 575 | V | 100 drops value; IEC 60112 |
Comparative Tracking Index | 600 | V | Test Solution A CTI; IEC 60112 |