myالوثائق الفنية
Description: VESTODUR X7329 is a glass fiber reinforced(30 %), self-extinguishing (V-0 at 1.6 mm) poly-butylene terephthalate (PBT) compound with a creamy-white color. The compound is suitable for the injection molding of parts with high mechanical and thermal resistance.
تفاصيل مركب
نوع المنتج
منتج
المورد
مزايا
- self-extinguishing
- high mechanical and thermal resistance
تطبيقات أخرى
the injection molding of parts with high mechanical and thermal resistance
معلومات تقنية
| كمية | قدر | وحدة | التعلیق |
|---|---|---|---|
| الخصائص الفيزيائية | |||
| Density | 1.67 | g/ml | ISO 1183 |
| Linear Mold Shrinkage | 0.002 | cm/cm | ;sheet with film gate at rim, mold temperature 80°C@Thickness 2.00 mm |
| Linear Mold Shrinkage | 0.018 | cm/cm | Transverse |
| الخصائص الحرارية | |||
| Flameability | IEC 60695@Thickness 1.60 mm | ||
| Vicat softening temperature | 220 | ºC | Method A, 10 N; ISO 306 |
| Glow WireTest | 960 | ºC | IEC 60695-2-1/0-3, @Thickness 2.00 mm |
| Vicat softening temperature | 213 | ºC | Method B, 50 N; ISO 306 |
| Flameability | IEC 60695@Thickness 0.800 mm | ||
| خصائص ميكانيكية | |||
| Charpy Impact Strength (notched) | 12 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |
| (Charpy Impact Strength(unnotched | 60 | kJ/m² | ISO 179/1eU@Temperature 23.0 °C |
| Elongation at break-MD | 2.3 | % | ISO 527-1/2 |
| Tensile Stress at yield-MD | 140 | MPa | ISO 527-1/2 |
| Tensile modulus-MD | 11000 | MPa | ISO 527-1/2 |
| Hardness Shore D | 84 | ISO 868 | |
| Charpy Impact Strength (notched) | 12 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
| (Charpy Impact Strength(unnotched | 60 | kJ/m² | ISO 179/1eU@Temperature -30.0 °C |
| الخواص الكيميائية | |||
| Electrolytic Corrosion | IEC 60426 | ||
| الخواص الكهربائية | |||
| Dissipation Factor | 0.015 | IEC 60250@Frequency 1e+6 Hz | |
| Comparative Tracking Index | 225 | V | 100 drops value; IEC 60112 |
| Comparative Tracking Index | 275 | V | Test Solution A CTI; IEC 60112 |
| Dielectric Strength | 31.0 | Kv/mm | K20/P50; IEC 60243-1 |
| Volume resistance | >1.00e+16 | ohm-cm | IEC 60093 |
| Dielectric Constant | 4.1 | IEC 60250@Frequency 100 Hz | |
| Dissipation Factor | 0.0030 | IEC 60250@Frequency 100 Hz | |
| Dielectric Constant | 4.4 | IEC 60250@Frequency 1e+6 Hz | |
| Surface Resistance | 1.00e+13 | ohm | IEC 60093 |