| MFI |
9 |
g/10min |
|
| Density |
1.04 |
g/ml |
|
| Glass transition Temperature |
89 |
ºC |
10°C/min (50°F/min) |
| Flameability |
|
|
HB@Thickness 1.60 mm |
| Flameability |
|
|
HB@Thickness 3.20 mm |
| Thermal Expansion |
<50 |
µm/m-°C |
@Temperature 20.0 °C |
| Heat Deflection temperature |
85 |
ºC |
at 0.46 MPa |
| Vicat softening temperature |
88 |
ºC |
50°C/hr/50 N |
| Heat Deflection temperature |
78 |
ºC |
at 1.8 MPa |
| Elongation at break-MD |
2 |
% |
|
| Tensile modulus-MD |
3200 |
MPa |
|
| (Charpy Impact Strength(unnotched |
10 |
kJ/m² |
|
| Tensile strength |
50 |
MPa |
|
| Oxirane Oxygen Content |
18 |
% |
|
| Moisture absorption |
0.0 |
% |
|
| Comparative Tracking Index |
350 |
V |
|
| Dielectric Strength |
65 |
Kv/mm |
|
| Dissipation Factor |
0.00020 |
|
@Frequency 1e+6 Hz |
| Electrical Resistivity |
>1.00e+15 |
ohm-cm |
|
| Surface Resistance |
1.00e+14 |
ohm |
|
| Dielectric Constant |
2 |
|
@Frequency 1e+6 Hz |
| Dissipation Factor |
0.00020 |
|
@Frequency 100 Hz |
| Dielectric Constant |
2 |
|
@Frequency 100 Hz |
my