MFI |
6 |
g/10min |
|
Density |
1.06 |
g/ml |
|
Heat Deflection temperature |
82 |
ºC |
at 1.8 MPa |
Vicat softening temperature |
92 |
ºC |
50°C/hr/50 N |
Thermal Expansion |
<50 |
µm/m-°C |
@Temperature 20.0 °C |
Heat Deflection temperature |
89 |
ºC |
at 0.46 MPa |
Flameability |
|
|
V-2@Thickness 1.60 mm |
Flameability |
|
|
V-2@Thickness 3.20 mm |
Charpy Impact Strength (notched) |
7 |
kJ/m² |
|
(Charpy Impact Strength(unnotched |
60 |
kJ/m² |
@Temperature -30.0 °C |
Elongation at yield |
1 |
% |
|
Tensile Stress at yield-MD |
30 |
MPa |
|
Elongation at break-MD |
40 |
% |
|
(Charpy Impact Strength(unnotched |
80 |
kJ/m² |
|
Tensile modulus-MD |
2400 |
MPa |
|
Moisture absorption |
0.0 |
% |
|
Oxirane Oxygen Content |
26 |
% |
|
Dissipation Factor |
0.00060 |
|
@Frequency 100 Hz |
Dissipation Factor |
0.00060 |
|
@Frequency 1e+6 Hz |
Comparative Tracking Index |
300 |
V |
|
Dielectric Constant |
2 |
|
@Frequency 1e+6 Hz |
Dielectric Constant |
2 |
|
@Frequency 100 Hz |
Electrical Resistivity |
>1.00e+15 |
ohm-cm |
|
Surface Resistance |
1.00e+14 |
ohm |
|
Dielectric Strength |
33 |
Kv/mm |
|