| MFI |
15 |
g/10min |
|
| Density |
1.06 |
g/ml |
|
| Heat Deflection temperature |
74 |
ºC |
at 1.8 MPa |
| Vicat softening temperature |
83 |
ºC |
50°C/hr/50 N |
| Thermal Expansion |
<50 |
µm/m-°C |
@Temperature 20.0 °C |
| Heat Deflection temperature |
82 |
ºC |
at 0.46 MPa |
| Flameability |
|
|
V-2@Thickness 1.60 mm |
| Flameability |
|
|
V-2@Thickness 3.20 mm |
| Charpy Impact Strength (notched) |
6 |
kJ/m² |
|
| (Charpy Impact Strength(unnotched |
50 |
kJ/m² |
@Temperature -30.0 °C |
| Elongation at yield |
1 |
% |
|
| Tensile Stress at yield-MD |
28 |
MPa |
|
| Elongation at break-MD |
35 |
% |
|
| (Charpy Impact Strength(unnotched |
65 |
kJ/m² |
|
| Tensile modulus-MD |
2400 |
MPa |
|
| Moisture absorption |
0.0 |
% |
|
| Oxirane Oxygen Content |
26 |
% |
|
| Dissipation Factor |
0.00060 |
|
@Frequency 100 Hz |
| Dissipation Factor |
0.00060 |
|
@Frequency 1e+6 Hz |
| Comparative Tracking Index |
300 |
V |
|
| Dielectric Constant |
2 |
|
@Frequency 1e+6 Hz |
| Dielectric Constant |
2 |
|
@Frequency 100 Hz |
| Electrical Resistivity |
>1.00e+15 |
ohm-cm |
|
| Surface Resistance |
1.00e+14 |
ohm |
|
| Dielectric Strength |
35 |
Kv/mm |
|