MFI |
3 |
g/10min |
|
Density |
1.04 |
g/ml |
|
Heat Deflection temperature |
86 |
ºC |
at 1.8 MPa |
Vicat softening temperature |
97 |
ºC |
50°C/hr/50 N |
Flameability |
|
|
HB@Thickness 3.20 mm |
Flameability |
|
|
HB@Thickness 1.60 mm |
Heat Deflection temperature |
94 |
ºC |
at 0.46 MPa |
Thermal Expansion |
<50 |
µm/m-°C |
@Temperature 20.0 °C |
Tensile modulus-MD |
2300 |
MPa |
|
(Charpy Impact Strength(unnotched |
90 |
kJ/m² |
|
Elongation at break-MD |
40 |
% |
|
Tensile Stress at yield-MD |
40 |
MPa |
|
Elongation at yield |
3 |
% |
|
(Charpy Impact Strength(unnotched |
70 |
kJ/m² |
@Temperature -30.0 °C |
Charpy Impact Strength (notched) |
8 |
kJ/m² |
|
Moisture absorption |
0.0 |
% |
|
Oxirane Oxygen Content |
18 |
% |
|
Dissipation Factor |
0.00030 |
|
@Frequency 100 Hz |
Dissipation Factor |
0.00030 |
|
@Frequency 1e+6 Hz |
Dielectric Strength |
62 |
Kv/mm |
|
Surface Resistance |
1.00e+14 |
ohm |
|
Electrical Resistivity |
>1.00e+15 |
ohm-cm |
|
Dielectric Constant |
2 |
|
@Frequency 100 Hz |
Dielectric Constant |
2 |
|
@Frequency 1e+6 Hz |
Comparative Tracking Index |
400 |
V |
|