PLEXIGLAS® 6N S000 is an amorphous thermoplastic molding compound (PMMA).
تفاصيل
صناعة
منتج
المورد
مزايا
- good flow
- high mechanical strength, surface hardness and mar resistance
- high light transmission
- excellent weather resistance
- free colorability due to crystal clarity
- complies to U.S. Pharmacopeia class VI
- very good mechanical properties
- high heat deflection temperature
- excellent flow / melt viscosity
تطبيقات أخرى
Particularly suitable for injection molding optical and technical items for medical applications (cuvettes)
معاملة
PLEXIGLAS® 6N S000 can be processed on injection molding machines with 3-zone general purpose screws for engineering thermoplastics.
PLEXIGLAS® molding compounds are supplied as pellets of uniform size, packaged in 25kg polyethylene bags or in 500kg boxes with PE lining; other packaging on request.
معلومات تقنية
| كمية | قدر | وحدة | التعلیق |
|---|---|---|---|
| خصائص المظهر | |||
| Refractive index | 1.49 | ISO 489;d=3 mm;589nm/23°C | |
| Appearance | |||
| الخصائص الفيزيائية | |||
| Melting range | 220 - 260 | ºC | |
| MVR | 12 | ml/10min | ISO 1133@Load 3.80 kg,Temperature 230 °C |
| Density | 1.19 | g/ml | ISO 1183 |
| الخصائص الحرارية | |||
| Vicat softening temperature | 96 | ºC | B50; ISO 306 |
| Thermal Expansion | 80 | µm/m-°C | ISO 11359 @Temperature 0-50°C |
| Flameability | IEC 60695-11-10@Thickness 1.60 mm | ||
| Dry Time | 120 - 180 | min | Desiccant-type drier |
| خصائص ميكانيكية | |||
| (Charpy Impact Strength(unnotched | 20 | kJ/m² | ISO 179/1eU@Temperature 23.0 °C |
| Tensile modulus-MD | 3200 | MPa | 1mm/min; ISO 527 |
| Strain at break-MD | 3 | % | 5mm/min; ISO 527 |
| Tensile Stress at break-MD | 67 | MPa | 5mm/min; ISO 527 |
| الخواص البصرية | |||
| Transmittance | 92 | % | ISO 13468-2;D65;d=3 mm |
| خصائص العملية | |||
| Mold Temperature | 60 - 90 | ºC | |
| Drying Temperature | <85 | ºC | Predrying |