Plexiglas® zk5HF Molding Compound

PLEXIGLAS® Resist zk5HF is an amorphous, impact-modified thermoplastic molding compound (PMMA-I). .Application: Used for injection molding as well as for extruding sheets and profiles.

تفاصيل

منتج
مزايا
  • high weather resistance
  • excellent transmission
  • claritybrilliant appearance
  • high break resistance
  • impact strength improved resistance to stress cracking
  • excellent flow
تطبيقات أخرى

extruding sheets and profiles
injection molding

معلومات تقنية

كمية قدر وحدة التعلیق
Processing Temperature 220 - 260 ºC Barrel Temperature
خصائص المظهر
Refractive index 1.49 ISO 489
الخصائص الفيزيائية
MFI 9.477 g/10min ISO 1133@Load 3.80 kg,Temperature 230 °C
Density 1.17 g/ml ISO 1183
Melting range 220 - 260 ºC
الخصائص الحرارية
Flameability IEC 707@Thickness 1.60 mm
Vicat softening temperature 96.0 ºC B50; ISO 306
Thermal Expansion 90.0 µm/m-°C ASTM E831 @Temperature 0.000 -50.0 °C
Dry Time 120 - 180 min Desiccant-type drier
خصائص ميكانيكية
Elongation at yield 4.5 % 50mm/min; ISO 527
(Charpy Impact Strength(unnotched 50 kJ/m² ISO 179@Temperature 23.0 °C
Tensile modulus-MD 2500 MPa 1mm/min; ISO 527
Elongation at break-MD 25 % ISO 527
Tensile Stress at yield-MD 55.0 MPa 50mm/min; ISO 527
الخواص الكيميائية
Water absorption 1.9 % Immersion; ISO 62;at Saturation
Moisture absorption 0.50 % 23°C, 50%; ISO 62; at Equilibrium
الخواص البصرية
Transmittance 92 % Transmission Factor; DIN 5036;Visible
خصائص العملية
Mold Temperature 50.0 - 70.0 ºC
Drying Temperature <85.0 ºC Predrying