الوثائق الفنية
PLEXIGLAS® Resist zk6BR is an amorphous, impact-modified thermoplastic molding compound (PMMA-I). Application: Used for extruding and coextruding sheets and profiles as well as for injection molding.
تفاصيل
منتج
المورد
مزايا
- high weather resistance
- excellent transmission
- claritybrilliant appearance
- maximum break resistance
- impact strength
- improved resistance to stress cracking
- balanced property profile
- AMECA listing
تطبيقات أخرى
extruding and coextruding sheets and profiles
injection molding
معلومات تقنية
كمية | قدر | وحدة | التعلیق |
---|---|---|---|
Processing Temperature | 220 - 260 | ºC | Barrel Temperature |
خصائص المظهر | |||
Refractive index | 1.49 | ISO 489 | |
الخصائص الفيزيائية | |||
MFI | 1.856 | g/10min | ISO 1133@Load 3.80 kg,Temperature 230 °C |
Density | 1.16 | g/ml | ISO 1183 |
Melting range | 220 - 260 | ºC | |
الخصائص الحرارية | |||
Dry Time | 120 - 180 | min | Desiccant-type drier |
Vicat softening temperature | 95.0 | ºC | B50; ISO 306 |
Heat Deflection temperature | 93.0 | ºC | ISO 75; at 0.46 MPa |
Heat Deflection temperature | 88.0 | ºC | ISO 75; at 1.8 MPa |
Thermal Expansion | 110 | µm/m-°C | ASTM E831 @Temperature 0.000 -50.0 °C |
Glass transition Temperature | 109 | ºC | IEC 10006 |
Flameability | IEC 707@Thickness 1.60 mm | ||
خصائص ميكانيكية | |||
Elongation at break-MD | 54 | % | ISO 527 |
(Charpy Impact Strength(unnotched | 80 | kJ/m² | ISO 179@Temperature 23.0 °C |
Elongation at yield | 5.0 | % | 50mm/min; ISO 527 |
Tensile modulus-MD | 1800 | MPa | 1mm/min; ISO 527 |
Tensile Stress at yield-MD | 45.0 | MPa | 50mm/min; ISO 527 |
الخواص الكيميائية | |||
Moisture absorption | 0.50 | % | 23°C, 50%; ISO 62; at Equilibrium |
Water absorption | 1.8 | % | Immersion; ISO 62;at Saturation |
الخواص البصرية | |||
Haze | <2.0 | % | ASTM D1003 |
Transmittance | 91 | % | Transmission Factor; DIN 5036;Visible |
خصائص العملية | |||
Drying Temperature | <85.0 | ºC | Predrying |
Mold Temperature | 50.0 - 70.0 | ºC |
اتصل بالمورد
للاتصال الموردين من هذه الماد وتسجيل طلب للحصول على سعر، عينة، التشاور أو قبل الفاتورة، يرجى ملء استمارة الطلب.