Technical Documents
Acrylonitrile butadiene styrene (ABS) /Polybutylene Terephthalate (PBT) alloy with 20% Glass Fiber. It is suitable for processing through injection molding.
Details Compound
CAS
9003-56-9, 65997-17-3, 24968-12-5 ;9003-54-7
Product Type
Reinforced with
Applications
Industry
Producer
Advantages
- General Purpose
Other Applications
Electric & Electronic Products (Speaker Frame)
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
dry Time | 4 - 5 | hr | |
Physical Properties | |||
Melting range | 240 - 250 | ºC | |
Humidity | <0.02 | % | |
Linear Mold Shrinkage | 0.0040 - 0.0090 | cm/cm | ASTM D955;(Flow), 3.2mm |
Specific Gravity | 1.35 | ASTM D792 | |
Thermal Properties | |||
Heat Deflection temperature | 160 | ºC | ASTM D648;6.4mm;(Unannealed);at 1.8 MPa |
Heat Deflection temperature | 195 | ºC | ASTM D648;6.4mm;(Unannealed);at 0.46 MPa |
Melting point | 225 | ºC | Peak at Break |
Mechanical Properties | |||
Izod impact strength (notched) | 63.7 | J/m | ASTM D256;23℃;3.2mm |
Flexural modulus-MD | 5690 | MPa | ASTM D790;1.3mm/min;3.2mm |
Flexural strength | 142 | MPa | ASTM D790;1.3mm/min;3.2mm;Yield |
Elongation at break-MD | 3 | % | ASTM D638;5mm/min;3.2mm |
Tensile Stress at yield-MD | 93.2 | MPa | ASTM D638;5mm/min;3.2mm |
Process Properties | |||
Drying Temperature | 100 | ºC | |
Mold Temperature | 60 - 80 | ºC | |
Middle Barrel Temperature | 230 - 245 | ºC |