starex® VG-4910 is a flame retardant acrylonitrile butadiene styrene (ABS) grade reinforced with 10 % glass fiber. Can be processed using injection molding.
Details Compound
Product Type
Reinforced with
Applications
Industry
Producer
Advantages
- excellent flexural modulus
- excellent heat resistance
- excellent dimensional stability
- high impact strength
- less changes in mechanical property over a wide temperature range
Other Applications
Appliances > Air conditioning
Automotive>interior
Electronics / Computers > television, monitor, OA machine
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Appearance Properties | |||
Appearance | Natural colors | ||
Physical state | Pill | ||
Physical Properties | |||
Shrinkage | 0.1 - 0.3 | % | (ISO 2577;Flow, 3.2 mm (MD |
Humidity | <0.05 | % | |
MFI | 23 | g/10min | ISO 1133;220℃/10kg |
Density | 1.12 | g/ml | ISO 1183 |
Thermal Properties | |||
Vicat softening temperature | 99 | ºC | ISO R 306;B/50 |
Heat Deflection temperature | 101 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Annealing |
Heat Deflection temperature | 97 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Annealing |
Dry Time | 120 - 180 | min | |
UL RTI | 60 | ºC | Mechanical without Impact, 1.6 mm, 2.5 mm, 3.0 mm |
UL RTI | 60 | ºC | Mechanical with Impact, 1.6 mm, 2.5 mm, 3.0 mm |
UL RTI | 60 | ºC | Electric, 1.6 mm, 2.5 mm, 3.0 mm |
Heat Deflection temperature | 101 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
Heat Deflection temperature | 92 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
Mechanical Properties | |||
Rockwell Hardness | 109 | ISO 2039-2;R Scale | |
Charpy Impact Strength (notched) | 7 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
(Izod impact strength(notched | 7 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
Flexural modulus-MD | 4100 | MPa | ISO 178;2mm/min |
Flexural strength | 100 | MPa | ISO 178;2mm/min |
Tensile Stress at break-MD | 75.51 | MPa | ISO 527;5mm/min |
Tensile modulus-MD | 3727 | MPa | ISO 527;5mm/min |
Strain at break-MD | 3.4 | % | ISO 527;5mm/min |
Tensile Stress at yield-MD | 85 | MPa | ISO 527;50mm/min |
Chemical Properties | |||
Decomposition temperature | >400 | ºC | |
Electrical Properties | |||
Hot Wire Ignition | 3 | s | 1.6mm, 3.0 mm |
HAI)High Amp Arc Ignition) | arcs | 1.6mm, 3.0 mm | |
Comparative Tracking Index | 2 | V |