mystarex® VG-4910 is a flame retardant acrylonitrile butadiene styrene (ABS) grade reinforced with 10 % glass fiber. Can be processed using injection molding.
Детали Соединение
Тип продукта
Усиленный с
Промышленность
Режиссер
Дреимущества
- excellent flexural modulus
- excellent heat resistance
- excellent dimensional stability
- high impact strength
- less changes in mechanical property over a wide temperature range
Другие приложения
Appliances > Air conditioning
Automotive>interior
Electronics / Computers > television, monitor, OA machine
Технические данные
| Количество | Стоимость | Е диница измерения | 3амечание |
|---|---|---|---|
| Свойства внешнего вида | |||
| Appearance | Natural colors | ||
| Physical state | Pill | ||
| Физические свойства | |||
| Shrinkage | 0.1 - 0.3 | % | (ISO 2577;Flow, 3.2 mm (MD |
| Humidity | <0.05 | % | |
| MFI | 23 | g/10min | ISO 1133;220℃/10kg |
| Density | 1.12 | g/ml | ISO 1183 |
| Тепловые свойства | |||
| Vicat softening temperature | 99 | ºC | ISO R 306;B/50 |
| Heat Deflection temperature | 101 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Annealing |
| Heat Deflection temperature | 97 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Annealing |
| Dry Time | 120 - 180 | min | |
| UL RTI | 60 | ºC | Mechanical without Impact, 1.6 mm, 2.5 mm, 3.0 mm |
| UL RTI | 60 | ºC | Mechanical with Impact, 1.6 mm, 2.5 mm, 3.0 mm |
| UL RTI | 60 | ºC | Electric, 1.6 mm, 2.5 mm, 3.0 mm |
| Heat Deflection temperature | 101 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
| Heat Deflection temperature | 92 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
| Механические свойства | |||
| Rockwell Hardness | 109 | ISO 2039-2;R Scale | |
| Charpy Impact Strength (notched) | 7 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
| (Izod impact strength(notched | 7 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
| Flexural modulus-MD | 4100 | MPa | ISO 178;2mm/min |
| Flexural strength | 100 | MPa | ISO 178;2mm/min |
| Tensile Stress at break-MD | 75.51 | MPa | ISO 527;5mm/min |
| Tensile modulus-MD | 3727 | MPa | ISO 527;5mm/min |
| Strain at break-MD | 3.4 | % | ISO 527;5mm/min |
| Tensile Stress at yield-MD | 85 | MPa | ISO 527;50mm/min |
| Химические свойства | |||
| Decomposition temperature | >400 | ºC | |
| Электрические свойства | |||
| Hot Wire Ignition | 3 | s | 1.6mm, 3.0 mm |
| HAI)High Amp Arc Ignition) | arcs | 1.6mm, 3.0 mm | |
| Comparative Tracking Index | 2 | V | |