ABS AF364 is a flame retardant acrylonitrile butadiene styrene(ABS) grade. It is suitable for processing through injection molding.
Details
Product Type
Applications
Industry
Producer
Advantages
- high fluidity
- good heat resistance
- enables cost reduction
- flame retardant
Other Applications
Electrical markets
Electronics / Computers > Housings
Electronics / Computers > Monitors
IT/OA device
television
VCRs
printers
fax machines
microwave ovens
digital cameras
camcorders
computers
CD-ROM bezels and adapters
automobile interior and exterior materials
housings for electric and electronic products
Handling
It is a RoHS compliant grade.
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| dry Time | 3 - 4 | hr | |
| Appearance Properties | |||
| Physical state | Pill | ||
| Physical Properties | |||
| Melting range | 200 - 230 | ºC | |
| Humidity | >0.01 | % | |
| MFI | 10 | g/10min | ASTM D1238;220℃/10kg |
| Shrinkage | 0.4 - 0.7 | % | ASTM D955;(Flow), 3.2mm |
| Specific Gravity | 1.19 | ASTM D792 | |
| Thermal Properties | |||
| UL RTI | 60 | ºC | UL 746B;Mechanical without Impact |
| UL RTI | 60 | ºC | UL 746B;Mechanical with Impact |
| UL RTI | 60 | ºC | UL 746B;Electrical |
| Flameability | UL94;3.0mm | ||
| Flameability | UL94;1.5mm | ||
| Flameability | UL94;2.0mm | ||
| Vicat softening temperature | 100 | ºC | ASTM D1525;5kg, 50℃/h |
| Heat Deflection temperature | 103 | ºC | ASTM D648;6.4mm;(Unannealed);4.6kg |
| Heat Deflection temperature | 93 | ºC | ASTM D648;6.4mm;(Unannealed);18.6kg |
| Mechanical Properties | |||
| Rockwell Hardness | 105 | ASTM D785;R-Scale | |
| Izod impact strength (notched) | 68.6 | J/m | ASTM D256;-30℃;3.2mm |
| Izod impact strength (notched) | 186.3 | J/m | ASTM D256;23℃;3.2mm |
| Flexural modulus-MD | 2354 | MPa | ASTM D790;15mm/min;6.4mm |
| Izod impact strength (notched) | 157 | J/m | ASTM D256;23℃;6.4mm |
| Izod impact strength (notched) | 49 | J/m | ASTM D256;-30℃;6.4mm |
| Flexural strength | 70.61 | MPa | ASTM D790;15mm/min;6.4mm |
| Tensile modulus-MD | 2157 | MPa | ASTM D638;1mm/min;3.2mm |
| Elongation at yield | 5 | % | ASTM D638;50mm/min;3.2mm |
| Elongation at break-MD | >20 | % | ASTM D638;50mm/min;3.2mm |
| Tensile Stress at yield-MD | 42.17 | MPa | ASTM D638;50mm/min;3.2mm |
| Process Properties | |||
| Middle Barrel Temperature | 180 - 200 | ºC | |
| Drying Temperature | 80 - 90 | ºC | |
| Mold Temperature | 40 - 60 | ºC | |