myTechnical Documents
ABS BM662B is a heat resistant acrylonitrile butadiene styrene (ABS)grade. It is suitable for processing through blow molding.
Details
Product Type
Applications
Producer
Advantages
- heat resistance
- Enables cost reduction
Other Applications
Automotive > Lighting
Automotive >Housings>spoiler, bumper guard
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Processing Temperature | 190 - 210 | ºC | Barrel Temperature;Zone 3 |
| Processing Temperature | 200 - 220 | ºC | Barrel Temperature;Zone 4 |
| Processing Temperature | 190 - 210 | ºC | Barrel Temperature;Zone 2 |
| Processing Temperature | 180 - 200 | ºC | Barrel Temperature;Zone 1 |
| dry Time | 3 - 4 | hr | |
| Appearance Properties | |||
| Physical state | Pill | ||
| Physical Properties | |||
| Melting range | 200 - 210 | ºC | |
| Humidity | <0.01 | % | |
| MFI | 2 | g/10min | ASTM D1238;220℃/10kg |
| Shrinkage | 0.4 - 0.7 | % | ASTM D955;(Flow), 3.2mm |
| Specific Gravity | 1.05 | ASTM D792 | |
| Thermal Properties | |||
| Heat Deflection temperature | 108 | ºC | ASTM D648;6.4mm;(Unannealed);4.6kg |
| Vicat softening temperature | 106 | ºC | ASTM D1525;5kg, 50℃/h |
| Heat Deflection temperature | 100 | ºC | ASTM D648;6.4mm;(Unannealed);18.6kg |
| Mechanical Properties | |||
| Rockwell Hardness | 101 | ASTM D785;R-Scale | |
| Izod impact strength (notched) | 68.65 | J/m | ASTM D256;-30℃;3.2mm |
| Izod impact strength (notched) | 127.5 | J/m | ASTM D256;23℃;3.2mm |
| Izod impact strength (notched) | 68.65 | J/m | ASTM D256;-30℃;6.4mm |
| Izod impact strength (notched) | 127.5 | J/m | ASTM D256;23℃;6.4mm |
| Flexural modulus-MD | 2108 | MPa | ASTM D790;15mm/min;6.4mm |
| Flexural strength | 70.61 | MPa | ASTM D790;15mm/min;6.4mm |
| Elongation at break-MD | 30 | % | ASTM D638;50mm/min;3.2mm |
| Tensile Stress at yield-MD | 45.11 | MPa | ASTM D638;50mm/min;3.2mm |
| Process Properties | |||
| Die Temperature | 220 | ºC | |
| Drying Temperature | 80 - 90 | ºC | |