Technical Documents
CYREX 953 alloy is an opaque, acrylic-polycarbonate alloy with an impact strength that is higher than polycarbonate.
Details Compound
Applications
Producer
Supplier
Advantages
- outstanding impact strength
- excellent toughness
- excellent processing characteristics
- very good chemical resistance
- good heat resistance
- high impact strength at cold temperature
- high melt flow rate
Other Applications
Used for injection molding and extrusion of both thin and thickwall applications.
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
Specific Gravity | 1.15 | ASTM D792 | |
Melting range | 238 - 266 | ºC | |
MFI | 1.9 | g/10min | ASTM D1238@Load 3.80 kg, Temperature 230 °C |
Bulk density | 0.650 | g/ml | ASTM D1895 |
Linear Mold Shrinkage | 0.0040 - 0.0080 | cm/cm | ASTM D951 |
Thermal Properties | |||
Thermal Expansion | 93.6 | µm/m-°C | linear;ASTM D696@Temperature 0.000 -100 °C |
Heat Deflection temperature | 103 | ºC | Annealed; ASTM D648@Thickness 6.35 mm; at 1.8 MPa |
Vicat softening temperature | 135 | ºC | ASTM D1525 |
Dry Time | 180 - 240 | min | |
Mechanical Properties | |||
Izod impact strength (notched) | 913 | J/m | BAR; ASTM D256@Diameter 6.35 mm,Temperature 0.000 °C |
Flexural strength | 86.2 | MPa | ASTM D790 |
Elongation at yield | 4.2 | % | ASTM D638 |
Flexural modulus-MD | 2070 | MPa | ASTM D790 |
Izod impact strength (notched) | 1390 | J/m | bar; ASTM D256@Diameter 3.17 mm |
Elongation at break-MD | 88 | % | ASTM D638 |
Tensile modulus-MD | 2070 | MPa | ASTM D638 |
Tensile Stress at break-MD | 54.2 | MPa | ASTM D638 |
Rockwell Hardness | 44 | Rockwell M; ASTM D785 | |
Chemical Properties | |||
Water absorption | <0.26 | % | ASTM D570 |
Optical Properties | |||
Transmittance | 0.0 | % | visible;Opaque; ASTM D1003 |
Process Properties | |||
Middle Barrel Temperature | 199 - 266 | ºC | Cylinder Temp |
Mold Temperature | 65.6 - 98.9 | ºC | |
Drying Temperature | 82.2 | ºC |