Technical Documents
Thermoplastic, low viscosity plastic resin for injection molding, compression molding and extrusion.
Details
Product Type
Applications
Producer
Supplier
Other Applications
Wire and cable jacketing
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
Density | 1.78 | g/ml | |
MFI | 15 | g/10min | |
Thermal Properties | |||
Thermal Expansion | 100 | µm/m-°C | Parallel to Flow@Temperature 20.0 °C |
Thermal Expansion | 100 | µm/m-°C | Transverse to Flow@Temperature 20.0 °C |
Heat Deflection temperature | 70 | ºC | at 1.8 MPa |
Heat Deflection temperature | 130 | ºC | at 0.46 MPa |
Vicat softening temperature | 166 | ºC | 50°C/hr/50 N |
Flameability | @Thickness 1.60 mm | ||
Mechanical Properties | |||
(Charpy Impact Strength(unnotched | 210 | kJ/m² | @Temperature -30.0 °C |
Elongation at break-MD | > 50 | % | |
Tensile strength | 55.0 | MPa | |
Tensile modulus-MD | 2100 | MPa | |
Elongation at yield | 8.0 | % | |
(Charpy Impact Strength(unnotched | 260 | kJ/m² | |
Charpy Impact Strength (notched) | 13 | kJ/m² | |
Charpy Impact Strength (notched) | 6 | kJ/m² | @Temperature -30.0 °C |
Tensile Impact strength | 140 | Kj/m² | |
Creep modulus | 1600 | MPa | 1hour |
Creep modulus | 950 | MPa | 1000hours |
Chemical Properties | |||
Water absorption | 0.00 | % | |
Electrical Properties | |||
Dielectric Strength | 22.0 | Kv/mm | |
Dielectric Constant | 9 | @Frequency 100 Hz | |
Dielectric Constant | 8.0 | @Frequency 1e+6 Hz | |
Dissipation Factor | 0.034 | @Frequency 100 Hz | |
Electrical Resistivity | 3.00e+13 | ohm-cm | |
Surface Resistance | > 1.00e+15 | ohm | |
Dissipation Factor | 0.24 | @Frequency 1e+6 Hz | |
Comparative Tracking Index | 275 | V |