myFarapol I 214 is an Unsaturated Polyester Resin based on Isophthalic Acid, Neopentyl Glycol and standard Glycols, dissolved in and cross linked with Styrene having capability to be used as casting and laminating resin for piping and items to be used in medium level abrasive environment.
Details
Isophthalic Acid, Neopentyl Glycol and standard Glycols
- Medium reactivity
- Good laminating & wetting properties
- Good corrosion resistance
- Low water absorption
- Outstanding resistance to hydrolysis
Manufacturing of vessels
High Quality Coating and Gel Coats
Structural Items
Farapol I 214 is a product sensitive to temperature, Light & Oxidation. Hence should be stored indoors in dry place at a temperature between 5 and 25°C. Keep always in the original,unopened and undamaged containers. Avoid keeping material exposed to sunlight.
Avoid storing the resin along with Metallic Driers and Peroxides in the same area.
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Appearance Properties | |||
| Color | <2 | Gardner | |
| Physical Properties | |||
| Shrinkage | Almost 1.4 | % | |
| Density | Approximately 1.12 | g/ml | |
| Solid Content | 60 ± 2 | % | |
| Viscosity | 350 ± 30 | cP | 25°C |
| Thermal Properties | |||
| Heat Deflection temperature | >85 | ºC | ISO527-2 |
| Mechanical Properties | |||
| barcol hardness | >40 | ASTM D2583 | |
| Tensile strength | >70 | MPa | ISO527-2 |
| Elongation at break-MD | >3 | % | ISO527-2 |
| Flexural strength | >135 | MPa | ISO178 |
| Chemical Properties | |||
| Gel time | 840 ± 120 | sec. | 25°C |
| Acidity number | <20 | mg KOH/g | |
| Water absorption | Almost 0.3 | % | ISO62- Test Method 3 |