myINFINO® GC-1015 is an eco-friendly, halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy based on 30 % post-consumer material (PCM).Can be processed using injection molding.
Details
Product Type
Applications
Industry
Producer
Advantages
- high impact strength & modulus
- high flowability
- good colorability
- excellent appearance
- well-balanced mechanical properties & processability
- halogen free
- flame retardant
- eco-friendly
Other Applications
Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Appearance Properties | |||
| Physical state | Pill | ||
| Appearance | Natural colors | ||
| Physical Properties | |||
| Humidity | <0.05 | % | |
| MFI | 43 | g/10min | ISO 1133;220℃/10kg |
| Shrinkage | 0.2 - 0.4 | % | (ISO 2577;Cross Flow, 3.2 mm (TD |
| Shrinkage | 0.2 - 0.3 | % | ISO 2577;Flow, 3.2 mm (MD) |
| Density | 1.18 | g/ml | ISO 1183 |
| Thermal Properties | |||
| UL RTI | 95 | ºC | Mechanical without Impact, 1.5 mm, 2.0 mm, 3.0 mm |
| UL RTI | 85 | ºC | Mechanical with Impact, 1.5 mm, 2.0 mm, 3.0 mm |
| UL RTI | 95 | ºC | Electric, 1.5 mm, 2.0 mm, 3.0 mm |
| Vicat softening temperature | 96 | ºC | ISO R 306;B/50 |
| Vicat softening temperature | 98 | ºC | ISO R 306;B/120 |
| Heat Deflection temperature | 90 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
| Heat Deflection temperature | 80 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
| Mechanical Properties | |||
| Rockwell Hardness | 116 | ISO 2039-2;R Scale | |
| Charpy Impact Strength (notched) | 15 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
| (Izod impact strength(notched | 50 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
| Flexural modulus-MD | 2600 | MPa | ISO 178;2mm/min |
| Flexural strength | 90 | MPa | ISO 178;2mm/min |
| Tensile Stress at break-MD | 50 | MPa | ISO 527;50mm/min |
| Tensile modulus-MD | 2500 | MPa | ISO 527;50mm/min |
| Strain at break-MD | 50 | % | ISO 527;50mm/min |
| Tensile Stress at yield-MD | 60 | MPa | ISO 527;50mm/min |
| Chemical Properties | |||
| Decomposition temperature | >400 | ºC | |
| Electrical Properties | |||
| Hot Wire Ignition | 2 | s | 1.5mm |
| HAI)High Amp Arc Ignition) | 3 | arcs | 1.5mm |