INFINO® GC-1150 is an eco-friendly, halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy based on 30 % post-consumer material (PCM).Can be processed using injection molding.
Details
Product Type
Applications
Industry
Producer
Advantages
- high impact strength & modulus
- high flowability
- good colorability
- excellent appearance
- well-balanced mechanical properties & processability
- halogen free
- flame retardant
- eco-friendly
Other Applications
Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Appearance Properties | |||
Appearance | Natural colors | ||
Physical state | Pill | ||
Physical Properties | |||
Humidity | <0.05 | % | |
Shrinkage | 0.22 - 0.27 | % | (ISO 2577;Flow, 3.2 mm (MD |
MFI | 31 | g/10min | ISO 1133;220℃/10kg |
Density | 1.29 | g/ml | ISO 1183 |
Shrinkage | 0.23 - 0.28 | % | (ISO 2577;Cross Flow, 3.2 mm (TD |
Thermal Properties | |||
UL RTI | 60 | ºC | Mechanical without Impact, 1.2 mm, 3.0 mm |
UL RTI | 60 | ºC | Mechanical with Impact, 1.2 mm, 3.0 mm |
UL RTI | 60 | ºC | Electric, 1.2 mm, 3.0 mm |
Vicat softening temperature | 93 | ºC | ISO R 306;B/50 |
Heat Deflection temperature | 83 | ºC | ASTM D648;18.56 kgf/cm2, 6.4 mm |
Mechanical Properties | |||
Charpy Impact Strength (notched) | 7 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
Flexural modulus-MD | 3900 | MPa | ISO 178;2mm/min |
(Izod impact strength(notched | 6 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
Flexural strength | 93 | MPa | ISO 178;2mm/min |
Tensile Stress at break-MD | 43.15 | MPa | ASTM D638;50mm/min |
Tensile modulus-MD | 4158 | MPa | ASTM D638;50mm/min |
Strain at break-MD | 11 | % | ISO 527;50mm/minASTM D638 |
Tensile Stress at yield-MD | 64 | MPa | ISO 527;50mm/min |
Chemical Properties | |||
Decomposition temperature | >400 | ºC |