INFINO® LS-1150G is a halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy reinforced with 15 % glass fiber. Can be processed using injection molding.
Details Compound
Product Type
Reinforced with
Applications
Industry
Producer
Advantages
- high impact strength & modulus
- high flowability
- good colorability
- excellent appearance
- well-balanced mechanical properties & processability
- halogen free
- flame retardant
Other Applications
mold frame for liquid-crystal display (LCD) BLU
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Appearance Properties | |||
Appearance | Natural colors | ||
Physical state | Pill | ||
Physical Properties | |||
Humidity | <0.05 | % | |
MFI | 24 | g/10min | ISO 1133;250℃/10kg |
Density | 1.28 | g/ml | ISO 1183 |
Thermal Properties | |||
Heat Deflection temperature | 128 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Annealing |
Heat Deflection temperature | 123 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Annealing |
Heat Deflection temperature | 122 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
Dry Time | 120 - 240 | min | |
UL RTI | 60 | ºC | Mechanical without Impact, 0.75 mm, 3.0 mm |
UL RTI | 60 | ºC | Mechanical with Impact, 0.75 mm, 3.0 mm |
UL RTI | 60 | ºC | Electric, 0.75 mm, 3.0 mm |
Vicat softening temperature | 130 | ºC | ISO R 306;B/120 |
Vicat softening temperature | 128 | ºC | ISO R 306;B/50 |
Heat Deflection temperature | 120 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
Mechanical Properties | |||
Rockwell Hardness | 121 | ISO 2039-2;R Scale | |
Charpy Impact Strength (notched) | 9.9 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
(Izod impact strength(notched | 8.2 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
Flexural modulus-MD | 4400 | MPa | ISO 178;2mm/min |
Flexural strength | 135 | MPa | ISO 178;2mm/min |
Tensile Stress at break-MD | 98 | MPa | ISO 527;50mm/min |
Tensile modulus-MD | 4500 | MPa | ISO 527;50mm/min |
Strain at break-MD | 3.6 | % | ISO 527;50mm/min |
Tensile Stress at yield-MD | 86 | MPa | ISO 527;50mm/min |
Chemical Properties | |||
Decomposition temperature | >400 | ºC |