INFINO® LS-1159S

INFINO® LS-1159S is a halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy reinforced with 15 % glass fiber. Can be processed using injection molding.

Details Compound

Product Type

Polymer > ABS
Polymer > Polycarbonate

Reinforced with

Additive > Reinforcers > Glass fiber

Applications

Polymers industry > Injection moulding

Industry

Electronics

Producer

Samsung

Advantages
  • high impact strength & modulus
  • high flowability
  • good colorability
  • excellent appearance
  • well-balanced mechanical properties & processability
  • halogen free
  • flame retardant
Other Applications

Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter

Technical data

Quantity Value Unit Comment
Appearance Properties
Appearance Natural colors
Physical state Pill
Physical Properties
Humidity <0.05 %
MFI 25 g/10min ISO 1133;220℃/10kg
MFI 9 g/10min ISO 1133;250℃/2.16kg
Shrinkage 0.1 % (ISO 2577;Cross Flow, 3.2 mm (TD
Shrinkage 0.1 % (ISO 2577;Flow, 3.2 mm (MD
Density 1.28 g/ml ISO 1183
Thermal Properties
Heat Deflection temperature 93 ºC ISO 75-2;0.45 MPa, 4.0 mm, Unannealed
Dry Time 180 - 240 min
UL RTI 60 ºC Mechanical without Impact, 1.5 mm, 2.0 mm, 2.5 mm, 3.0 mm
Vicat softening temperature 95 ºC ISO R 306;B/50
UL RTI 60 ºC Electric, 1.5 mm, 2.0 mm, 2.5 mm, 3.0 mm
UL RTI 60 ºC Mechanical with Impact, 1.5 mm, 2.0 mm, 2.5 mm, 3.0 mm
Heat Deflection temperature 90 ºC ISO 75-2;1.8 MPa, 4.0 mm, Unannealed
Mechanical Properties
Rockwell Hardness 120 ISO 2039-2;R Scale
(Izod impact strength(notched 8 kJ/m² ISO 180 1A;at 23°C, 4 mm
Charpy Impact Strength (notched) 8 kJ/m² ISO 179 1eA;at 23°C, 4 mm
Flexural modulus-MD 4500 MPa ISO 178;2.8mm/min
Flexural strength 120 MPa ISO 178;2.8mm/min
Tensile Stress at break-MD 90 MPa ISO 527;5mm/min
Tensile modulus-MD 4000 MPa ISO 527;5mm/min
Strain at break-MD 3 % ISO 527;5mm/min
Tensile Stress at yield-MD 90 MPa ISO 527;5mm/min
Chemical Properties
Decomposition temperature >400 ºC