myINFINO® NE-1050 is a halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy. Can be processed using injection molding.
Details
Product Type
Applications
Industry
Producer
Advantages
- high impact strength & modulus
- high flowability
- good colorability
- excellent appearance
- well-balanced mechanical properties & processability
- halogen free
- flame retardant
Other Applications
Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Appearance Properties | |||
| Appearance | Natural colors | ||
| Physical state | Pill | ||
| Physical Properties | |||
| Humidity | <0.05 | % | |
| MFI | 40 | g/10min | ISO 1133;220℃/10kg |
| Shrinkage | 05 - 0.7 | % | (ASTM D955;Flow, 3.2 mm (MD |
| Density | 1.19 | g/ml | ISO 1183 |
| Thermal Properties | |||
| Heat Deflection temperature | 99 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Annealing |
| Heat Deflection temperature | 96 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Annealing |
| Heat Deflection temperature | 95 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
| Dry Time | 240 - 360 | min | |
| Dry Time | 120 - 240 | min | |
| UL RTI | 60 | ºC | Mechanical without Impact, 1.5 mm, 2.0 mm, 3.0 mm |
| UL RTI | 60 | ºC | Mechanical with Impact, 1.5 mm, 2.0 mm, 3.0 mm |
| UL RTI | 60 | ºC | Electric, 1.5 mm, 2.0 mm, 3.0 mm |
| Vicat softening temperature | 104 | ºC | ISO R 306;B/120 |
| Vicat softening temperature | 100 | ºC | ISO R 306;B/50 |
| Heat Deflection temperature | 84 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
| Mechanical Properties | |||
| Rockwell Hardness | 120 | ISO 2039-2;R Scale | |
| Charpy Impact Strength (notched) | 20 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
| Izod impact strength (notched) | 490.3 | J/m | ASTM D256;at 23°C, 1/8 inch |
| Flexural modulus-MD | 2400 | MPa | ISO 178;2mm/min |
| Flexural strength | 83 | MPa | ISO 178;2mm/min |
| Tensile Stress at break-MD | 49 | MPa | ISO 527;50mm/min |
| Tensile modulus-MD | 2300 | MPa | ISO 527;50mm/min |
| Strain at break-MD | 51 | % | ISO 527;50mm/min |
| Tensile Stress at yield-MD | 58 | MPa | ISO 527;50mm/min |
| Chemical Properties | |||
| Decomposition temperature | >400 | ºC | |