INFINO® NH-1001T

Technical Documents

INFINO® NH-1001T is a halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy. Can be processed using injection molding.

Details

Product Type

Polymer > ABS
Polymer > Polycarbonate

Applications

Polymers industry > Injection moulding

Industry

Electronics

Producer

Samsung

Advantages
  • high impact strength & modulus
  • high flowability
  • good colorability
  • excellent appearance
  • well-balanced mechanical properties & processability
  • halogen free
  • flame retardant
Other Applications

Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter

Technical data

Quantity Value Unit Comment
Appearance Properties
Appearance Natural colors
Physical state Pill
Physical Properties
Humidity <0.05 %
MFI 25 g/10min ISO 1133;220℃/10kg
Density 1.16 g/ml ISO 1183
Thermal Properties
Heat Deflection temperature 88 ºC ISO 75-2;0.45 MPa, 4.0 mm, Unannealed
Dry Time 240 - 360 min
Dry Time 120 - 240 min
UL RTI 60 ºC Mechanical without Impact, 1.5 mm, 2.0 mm, 3.0 mm
UL RTI 60 ºC Mechanical with Impact, 1.5 mm, 2.0 mm, 3.0 mm
UL RTI 60 ºC Electric, 1.5 mm, 2.0 mm, 3.0 mm
Vicat softening temperature 95 ºC ISO R 306;B/120
Vicat softening temperature 93 ºC ISO R 306;B/50
Heat Deflection temperature 77 ºC ISO 75-2;1.8 MPa, 4.0 mm, Unannealed
Mechanical Properties
Rockwell Hardness 114 ISO 2039-2;R Scale
Charpy Impact Strength (notched) 60 kJ/m² ISO 179 1eA;at 23°C, 4 mm
(Izod impact strength(notched 55 kJ/m² ISO 180 1A;at 23°C, 4 mm
Flexural modulus-MD 2300 MPa ISO 178;2mm/min
Flexural strength 83 MPa ISO 178;2mm/min
Tensile Stress at break-MD 52 MPa ISO 527;50mm/min
Tensile modulus-MD 2300 MPa ISO 527;50mm/min
Strain at break-MD 99 % ISO 527;50mm/min
Tensile Stress at yield-MD 55 MPa ISO 527;50mm/min
Chemical Properties
Decomposition temperature >400 ºC