INFINO® NH-1015

Technical Documents

INFINO® NH-1015 is a halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy.Can be processed using injection molding.

Details

Product Type

Polymer > ABS
Polymer > Polycarbonate

Applications

Polymers industry > Injection moulding

Industry

Electronics

Producer

Samsung

Advantages
  • high impact strength & modulus
  • high flowability
  • good colorability
  • excellent appearance
  • well-balanced mechanical properties & processability
  • halogen free
  • flame retardant
Other Applications

Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter

Technical data

Quantity Value Unit Comment
Appearance Properties
Appearance Natural colors
Physical state Pill
Physical Properties
Humidity <0.05 %
Density 1.18 g/ml ISO 1183
MFI 23 g/10min ISO 1133;220℃/10kg
Thermal Properties
Glow WireTest 800 ºC Glow Wire Ignition Temperature;IEC 60695-2-13;1.3 mm, 2.1 mm, 2.5 mm, 3.0 mm
Glow WireTest 775 ºC Glow Wire Ignition Temperature;IEC 60695-2-13;1.0 mm, 1.5 mm
Glow WireTest 960 ºC Glow Wire Flammability Index;IEC 60695-2-12;1.0 mm, 1.3 mm, 1.5 mm, 2.1 mm, 2.5 mm, 3.0 mm
UL RTI 90 ºC Mechanical without Impact, 1.5 mm, 2.0 mm, 2.1 mm, 2.5 mm, 3.0 mm
UL RTI 85 ºC Mechanical with Impact, 1.5 mm, 2.0 mm, 2.1 mm, 2.5 mm, 3.0 mm
UL RTI 90 ºC Electric, 1.5 mm, 2.0 mm, 2.1 mm, 2.5 mm, 3.0 mm
Heat Deflection temperature 98 ºC ISO 75-2;0.45 MPa, 4.0 mm, Annealing
Heat Deflection temperature 93 ºC ISO 75-2;1.8 MPa, 4.0 mm, Annealing
Heat Deflection temperature 93 ºC ISO 75-2;0.45 MPa, 4.0 mm, Unannealed
Dry Time 240 - 360 min
Dry Time 120 - 240 min
UL RTI 60 ºC Mechanical without Impact, 1.0 mm, 1.2 mm, 1.3 mm
UL RTI 60 ºC Mechanical with Impact, 1.0 mm, 1.2 mm, 1.3 mm
Vicat softening temperature 100 ºC ISO R 306;B/120
UL RTI 60 ºC Electric, 1.0 mm, 1.2 mm, 1.3 mm
Vicat softening temperature 98 ºC ISO R 306;B/50
Heat Deflection temperature 81 ºC ISO 75-2;1.8 MPa, 4.0 mm, Unannealed
Mechanical Properties
Rockwell Hardness 118 ISO 2039-2;R Scale
Charpy Impact Strength (notched) 44 kJ/m² ISO 179 1eA;at 23°C, 4 mm
(Izod impact strength(notched 40 kJ/m² ISO 180 1A;at 23°C, 4 mm
Flexural strength 88 MPa ISO 178;2mm/min
Flexural modulus-MD 2450 MPa ISO 178;2mm/min
Tensile Stress at break-MD 48 MPa ISO 527;50mm/min
Tensile Stress at yield-MD 60 MPa ISO 527;50mm/min
Tensile modulus-MD 2500 MPa ISO 527;50mm/min
Chemical Properties
Decomposition temperature >400 ºC
Electrical Properties
HAI)High Amp Arc Ignition) 3 arcs 1.5mm
Comparative Tracking Index V
Hot Wire Ignition 2 s 1.5mm