Technical Documents
INFINO® NH-1017SG is a halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy.Can be processed using injection molding.
Details
Product Type
Applications
Industry
Producer
Advantages
- high impact strength & modulus
- high flowability
- good colorability
- excellent appearance
- well-balanced mechanical properties & processability
- halogen free
- flame retardant
Other Applications
Electronics / Computers > TV housings ( liquid-crystal display (LCD) TV front cover)
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Appearance Properties | |||
Appearance | Natural colors | ||
Physical state | Pill | ||
Physical Properties | |||
Shrinkage | 0.31 - 0.38 | % | (ISO 2577;Cross Flow, 3.2 mm (TD |
Shrinkage | 0.29 - 0.36 | % | (ISO 2577;Flow, 3.2 mm (MD |
Humidity | <0.04 | % | |
MFI | 48 | g/10min | ISO 1133;220℃/10kg |
Density | 1.2 | g/ml | ISO 1183 |
Thermal Properties | |||
Heat Deflection temperature | 97 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Annealing |
Heat Deflection temperature | 91 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Annealing |
Heat Deflection temperature | 94 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
Dry Time | 240 | min | |
UL RTI | 60 | ºC | Mechanical without Impact, 0.8 mm, 1.0 mm, 1.5 mm, 3.0 mm |
UL RTI | 60 | ºC | Mechanical with Impact, 0.8 mm, 1.0 mm, 1.5 mm, 3.0 mm |
UL RTI | 60 | ºC | Electric, 0.8 mm, 1.0 mm, 1.5 mm, 3.0 mm |
Vicat softening temperature | 103 | ºC | ISO R 306;B/120 |
Vicat softening temperature | 100 | ºC | ISO R 306;B/50 |
Heat Deflection temperature | 84 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
Mechanical Properties | |||
Rockwell Hardness | 123 | ISO 2039-2;R Scale | |
Charpy Impact Strength (notched) | 6 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
(Izod impact strength(notched | 8 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
Flexural modulus-MD | 2900 | MPa | ISO 178;2mm/min |
Flexural strength | 100 | MPa | ISO 178;2mm/min |
Tensile Stress at break-MD | 50 | MPa | ISO 527;50mm/min |
Tensile modulus-MD | 2600 | MPa | ISO 527;50mm/min |
Strain at break-MD | 14 | % | ISO 527;50mm/min |
Tensile Stress at yield-MD | 68 | MPa | ISO 527;50mm/min |
Chemical Properties | |||
Decomposition temperature | >400 | ºC |