INFINO® NH-1022

INFINO® NH-1022 is a halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy.Can be processed using injection molding.

Details

Product Type

Polymer > ABS
Polymer > Polycarbonate

Applications

Polymers industry > Injection moulding

Industry

Electronics

Producer

Samsung

Advantages
  • high impact strength & modulus
  • high flowability
  • good colorability
  • excellent appearance
  • well-balanced mechanical properties & processability
  • halogen free
  • flame retardant
Other Applications

Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter

Technical data

Quantity Value Unit Comment
Appearance Properties
Appearance Natural colors
Physical state Pill
Physical Properties
Shrinkage 0.35 - 0.44 % (ISO 2577;Cross Flow, 3.2 mm (TD
Shrinkage 0.35 - 0.44 % (ISO 2577;Flow, 3.2 mm (MD
Humidity <0.05 %
MFI 19 g/10min ISO 1133;220℃/10kg
Density 1.19 g/ml ISO 1183
Thermal Properties
Auto-ignition temperature >400 ºC
Dry Time 240 - 360 min
Dry Time 120 - 240 min
UL RTI 60 ºC Mechanical without Impact, 0.8 mm, 3.0 mm
UL RTI 60 ºC Mechanical with Impact, 0.8 mm, 3.0 mm
UL RTI 60 ºC Electric, 0.8 mm, 3.0 mm
Vicat softening temperature 109 ºC ISO R 306;B/50
Heat Deflection temperature 107 ºC ISO 75-2;0.45 MPa, 4.0 mm, Unannealed
Heat Deflection temperature 104 ºC ISO 75-2;1.8 MPa, 4.0 mm, Unannealed
Mechanical Properties
Rockwell Hardness 119 ISO 2039-2;R Scale
Charpy Impact Strength (notched) 60 kJ/m² ISO 179 1eA;at 23°C, 4 mm
(Izod impact strength(notched 60 kJ/m² ISO 180 1A;at 23°C, 4 mm
Flexural modulus-MD 2300 MPa ISO 178;2mm/min
Flexural strength 90 MPa ISO 178;2mm/min
Tensile Stress at break-MD 60 MPa ISO 527;50mm/min
Tensile modulus-MD 2000 MPa ISO 527;50mm/min
Strain at break-MD 50 % ISO 527;50mm/min
Tensile Stress at yield-MD 62 MPa ISO 527;50mm/min