myINFINO® VB-3100G is a halogenated, flame retardant, low warpage polybutylene terephthalate (PBT) and acrylonitrile butadiene styrene (ABS) alloy reinforced with glass fiber. Can be processed using injection molding.
Details Compound
Product Type
Reinforced with
Applications
Industry
Producer
Advantages
- low warpage
- flame retardant
Other Applications
Electronics / Computers > TV housings,note PC
Telecom > Cellular phones
Appliances > Coffee makers
Automotive
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Appearance Properties | |||
| Appearance | Natural colors | ||
| Physical state | Pill | ||
| Physical Properties | |||
| Shrinkage | 0.6 - 1.2 | % | (ISO 2577;Flow, 3.2 mm (MD |
| Humidity | <0.05 | % | |
| MFI | 30 | g/10min | ISO 1133;250℃/2.16kg |
| Density | 1.45 | g/ml | ISO 1183 |
| Thermal Properties | |||
| Auto-ignition temperature | >400 | ºC | |
| Dry Time | 240 - 360 | min | |
| Dry Time | 120 - 240 | min | |
| UL RTI | 75 | ºC | Mechanical without Impact, 1.5 mm, 3.0 mm |
| UL RTI | 75 | ºC | Mechanical with Impact, 1.5 mm, 3.0 mm |
| UL RTI | 75 | ºC | Electric, 1.5 mm, 3.0 mm |
| Vicat softening temperature | 151 | ºC | ISO R 306;B/120 |
| Vicat softening temperature | 147 | ºC | ISO R 306;B/50 |
| Heat Deflection temperature | 125 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
| Mechanical Properties | |||
| Rockwell Hardness | 113 | ISO 2039-2;R Scale | |
| (Izod impact strength(notched | 4 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
| Flexural modulus-MD | 3500 | MPa | ISO 178;2mm/min |
| Flexural strength | 90 | MPa | ISO 178;2mm/min |
| Strain at break-MD | 4 | % | ISO 527;5mm/min |
| Tensile Stress at yield-MD | 70 | MPa | ISO 527;5mm/min |
| Chemical Properties | |||
| Water absorption | 0.08 | % | ISO 62;23°C |
| Electrical Properties | |||
| Comparative Tracking Index | 2 | V | |
| Hot Wire Ignition | s | 3.0mm | |
| HAI)High Amp Arc Ignition) | arcs | 3.0mm | |