myDetails
Product Type
Applications
Producer
Advantages
- High strength
- Superior transparency and processability
- good appearance
- non-toxicity
- Excellent electrical properties
- Heat resistance and chemical resistance
- Superior extrusion processing
Other Applications
suitable for OPS, PSP and synthetic wood
food receptacles
stationery
audio tapes
toys
PSP sheet
film
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Physical Properties | |||
| Density | 1.05 | g/ml | ASTM D792 |
| Linear Mold Shrinkage | 0.004 - 0.008 | cm/cm | ASTM D955 |
| MFI | 3.5 | g/10min | Temperature 200 °C, Load 5 kg, ASTM D 1238 |
| Thermal Properties | |||
| Heat Deflection temperature | 85 | ºC | Thickness 0.5 in, 1.8 MPa (264 psi),Unannealed; ASTM D648 |
| Vicat softening temperature | 103 | ºC | 1000 g; ASTM D 1525 |
| Flameability | UL94, 1/16 in, 1/8 in | ||
| Mechanical Properties | |||
| Elongation at break-TD | 4 | % | 50 mm/min ; ASTM D638 |
| Tensile strength | 48.1 | MPa | Yield, 50 mm/min; ASTM D638 |
| Flexural modulus-MD | 3100 | MPa | 15 mm/min; ASTM D 790 |
| Flexural strength | 91.3 | MPa | Yield, 15 mm/min; ASTM D 790 |
| Rockwell Hardness | 120 | ASTM D 785 | |
| Electrical Properties | |||
| Hot Wire Ignition | 15 - 30 | s | UL Rating PLC 3 (15-30 sec), HWI |
| HAI)High Amp Arc Ignition) | >120 | arcs | UL Rating PLC 0 (>120 arcs), HAI |
| Comparative Tracking Index | 400 - 600 | V | UL Rating PLC 1 (400-600 volts) |
| Arc Resistance | 120 - 180 | s | UL Rating PLC 5 (120-180 sec) |