myDetails
Product Type
Applications
Producer
Advantages
- Heat resistance
- Balanced mechanical properties
- Good surface appearance with high gloss
- Excellent processability
Other Applications
TV sets
tape recorders
vacuum cleaners
washing machines
air conditioners
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Physical Properties | |||
| Density | 1.04 | g/ml | ASTM D792 |
| Linear Mold Shrinkage | 0.004 - 0.008 | cm/cm | ASTM D955 |
| MFI | 4 | g/10min | Temperature 200 °C, Load 5 kg, ASTM D 1238 |
| Thermal Properties | |||
| Heat Deflection temperature | 81 | ºC | Thickness 0.5 in,1.8 MPa (264 psi), Unannealed; ASTM D648 |
| Vicat softening temperature | 101 | ºC | 1000 g; ASTM D 1525 |
| Flameability | 1.16,1/8 in | ||
| Mechanical Properties | |||
| Tensile strength | 28.5 | MPa | 50 mm/min ; ASTM D638 |
| Flexural strength | 46.2 | MPa | Yield, 15 mm/min; ASTM D 790 |
| Flexural modulus-MD | 2100 | MPa | 15 mm/min; ASTM D 790 |
| Elongation at break-TD | 60 | % | 50 mm/min; ASTM D638 |
| Rockwell Hardness | 99 | ASTM D 785 | |
| Izod impact strength (notched) | 118 | J/m | Thickness 0.125, ASTM D256 |
| Izod impact strength (notched) | 83 | J/m | Thickness 0.25,ASTM D256 |
| Electrical Properties | |||
| Hot Wire Ignition | 15 - 30 | s | UL Rating PLC 3 (15-30 sec) |
| HAI)High Amp Arc Ignition) | >120 | arcs | UL Rating PLC 0 (>120 arcs) |
| Comparative Tracking Index | >600 | V | UL Rating PLC 0 (>600 volts) |
| Arc Resistance | 120 - 180 | s | UL Rating PLC 5 (120-180 sec) |