myTechnical Documents
PS, Flame Retardant.
Details
CAS
9003-55-8, 25713-60-4, 1309-64-4
Product Type
Producer
Other Applications
Parts of Printer or Copier
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Physical Properties | |||
| Humidity | <0.01 | % | injection molding |
| MFI | 11 | g/10min | Temperature 200 °C, Load 5 kg, ASTM D 1238 |
| Specific Gravity | 1.1 | ASTM D792 | |
| Linear Mold Shrinkage | 0.004 - 0.008 | cm/cm | Thickness 3.2 mm, ASTM D955 |
| Melting range | 200 - 230 | ºC | injection molding |
| Thermal Properties | |||
| Dry Time | 180 - 240 | min | injection molding |
| Heat Deflection temperature | 85 | ºC | Unannealed; ASTM D648, 0.46 MPa (66 psi) |
| Vicat softening temperature | 85 | ºC | 50°C/h; ASTM D 1525, Load 5 kg |
| UL RTI | 50 | ºC | Thickness 1.5,2.5,3 mm, Electrical |
| UL RTI | 50 | ºC | Thickness 1.5,2.5,3 mm, Mechanical with Impact |
| UL RTI | 50 | ºC | Thickness 1.5,2.5,3 mm, Mechanical without Impact |
| Flameability | Thickness 1.5,2.5,3 mm | ||
| Mechanical Properties | |||
| Elongation at yield | >5 | % | Thickness 3.2 mm, 50 mm/min ; ASTM D638 |
| Tensile strength | 32.3 | MPa | Yield, Thickness 3.2 mm, 50 mm/min ; ASTM D638 |
| Elongation at break-MD | 50 | % | Thickness 3.2 mm, 50 mm/min ; ASTM D638 |
| Flexural strength | 51.9 | MPa | Yield, Thickness 3.2 mm, 15 mm/min; ASTM D 790 |
| Flexural modulus-MD | 2451.6 | MPa | Thickness 3.2 mm, 15 mm/min; ASTM D 790 |
| Rockwell Hardness | 103 | ASTM D 785 | |
| Process Properties | |||
| Mold Temperature | 40 - 60 | ºC | injection molding |
| Drying Temperature | 60 - 70 | ºC | injection molding |
| Middle Barrel Temperature | 190 - 200 | ºC | injection molding |