Technical Documents
PS, Flame Retardant.
Details
CAS
9003-55-8, 25713-60-4, 1309-64-4
Product Type
Producer
Other Applications
Parts of Printer or Copier
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
Humidity | <0.01 | % | injection molding |
MFI | 11 | g/10min | Load 5 kg, Temperature 200 °C, ASTM D 1238 |
Specific Gravity | 1.16 | ASTM D792 | |
Linear Mold Shrinkage | 0.004 - 0.008 | cm/cm | ASTM D955 |
Melting range | 200 - 230 | ºC | injection molding |
Thermal Properties | |||
Dry Time | 180 - 240 | min | injection molding |
Heat Deflection temperature | 77 | ºC | Unannealed; ASTM D648, Thickness 6.4 mm, 1.8 MPa (264 psi) |
Vicat softening temperature | 85 | ºC | Load 5 kg, 50°C/h; ASTM D 1525 |
UL RTI | 50 | ºC | Thickness 1.5,2.5,3 mm, Electrical |
Heat Deflection temperature | 85 | ºC | Unannealed; ASTM D648, 0.46 MPa (66 psi) |
UL RTI | 50 | ºC | Thickness 1.5,2.5,3 mm, Mechanical without Impact |
UL RTI | 50 | ºC | Thickness 1.5,2.5,3 mm, Mechanical with Impact |
Flameability | Thickness 1.5,2.5,3 mm, UL94 | ||
Mechanical Properties | |||
Elongation at yield | >5 | % | Thickness 3.2 mm, 50 mm/min ; ASTM D638 |
Tensile strength | 39.2 | MPa | Yield, Thickness 3.2 mm, 50 mm/min ; ASTM D638 |
Elongation at break-MD | 60 | % | Thickness 3.2 mm, 50 mm/min ; ASTM D638 |
Flexural strength | 39.2 | MPa | Yield, Thickness 3.2 mm, 15 mm/min; ASTM D 790 |
Flexural modulus-MD | 2255.5 | MPa | Thickness 3.2 mm, 15 mm/min; ASTM D 790 |
Rockwell Hardness | 90 | ASTM D 785 | |
Process Properties | |||
Mold Temperature | 40 - 60 | ºC | injection molding |
Drying Temperature | 60 - 70 | ºC | injection molding |
Middle Barrel Temperature | 190 - 200 | ºC | injection molding |